研究了绝缘包覆、压制成型、退火处理对软磁Fe-Si-Al磁粉芯性能的影响.采用扫描电镜,金相显微镜,B-H分析仪和万能材料试验机检测样品的内部结构、形貌、磁性能和力学性能.研究结果表明,添加绝缘剂能够有效的降低磁粉芯的涡流损耗;增大成型压力可以提高磁粉芯的压渍强度、密度、磁导率,降低损耗和矫顽力,最佳成型压力为1800MPa;压制后的退火处理是保证磁粉芯具有较好磁性能的关键,提高热处理温度可以有效的提高磁导率,降低磁滞损耗,但过高的热处理温度会使磁粉芯的磁性能恶化,最佳的退火温度为660℃.
参考文献
| [1] | Slama J.;Gruskova A. .Magnetic powder filled polymers[J].IEEE Transactions on Magnetics,1994(2):1101-1103. |
| [2] | Nowosielski R;Wyslocki J J;Wnuk I et al.[J].Journal of Materials Processing Technology,2006,175:324-329. |
| [3] | 王红忠,易健宏,彭元东,叶途明.2Mo81Ni17Fe磁粉芯磁导率的工艺影响因素[J].粉末冶金工业,2007(02):1-4. |
| [4] | 汪贵琴 .[J].粉末冶金工业,1998,8:26-29. |
| [5] | 姚丽姜;姚中;虞伟扬 .[J].上海钢研,2005,3:56-57. |
| [6] | Shokrollahi H;Janghorban K .[J].Journal of Magnetism and Magnetic Materials,2007,313:182-186. |
| [7] | Lefebvre L P;Pelletier S;Gelinas C .[J].J MagnMagn Mater,1997,176:193-196. |
| [8] | Kim Y B;Jang D H;Seok H K et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,449-451:389-393. |
| [9] | Shokrollahi H;Janghorban K .[J].Materials Science and Engineering B:Solid State Materials for Advanced Technology,2006,134:41-43. |
| [10] | Anhah M;Weidenfeller B .[J].Journal of Applied Physics,2007,101:023907. |
| [11] | Morrish A;Yu S .[J].Journal of Applied Physics,1955,26:1049. |
| [12] | Gibert I P;Moorthy V;Bull S J et al.[J].J MagnMagn Mater,2002,242-245:232-234. |
| [13] | Gilbert I.;Bull S.;Evans T.;Jack A.;Stephenson D.;De Sa A. .Effects of processing upon the properties of soft magnetic composites for low loss applications[J].Journal of Materials Science,2004(2):457-461. |
| [14] | Chieinas I;Geoffroy O;Isnard O et al.[J].J MagnMagn Mater,2005,290-291:1531-1534. |
| [15] | Hemmati I;Madaah Hosseini H R;Miraghaei S .[J].Powder Metallurgy,2007,50:86-90. |
| [16] | Prince S A;Oakley J .[J].Powder Metallurgy,1963,12:87. |
| [17] | Shokrollahi H;Janghorban K .[J].Journal of Magnetism and Magnetic Materials,2007,317:61-67. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%