采用光学显微镜、EBSD测试技术和三维原子探针分别对超低碳烘烤硬化钢的微观组织、织构以及固溶元素进行分析.结果表明,超低碳烘烤硬化钢经过750 ～ 810℃退火后,退火组织均为等轴状的铁素体组织,退火织构主要为{111}有利织构.随着退火温度的增加,其晶粒尺寸和{111}织构的强度都不断增大.烘烤硬化钢板经过退火后碳和磷元素在晶界等缺陷处发生了不同程度的偏聚.通过三维原子探针相应的软件计算得出,固溶在钢中的含碳量随着退火温度的增加而增大.
参考文献
| [1] | 关小军.超低碳高强度烘烤硬化钢[M].济南:山东科学技术出版社,2000:10-15. |
| [2] | CHEN Ji-ping,KANG Yong-lin,HAO Ying-min,LIU Guang-ming,XIONG Ai-ming.Microstructure and Properties of Ti and Ti+Nb Ultra-Low-Carbon Bake Hardened Steels[J].钢铁研究学报（英文版）,2009(06):33-40. |
| [3] | Jeong W C .Relationship between mechanical properties and microstructure in a 1.5％ Mn-0.3％ Mo ultra-low carbon steel with bake hardening[J].Materials Letters,2007,61:2579-2583. |
| [4] | Xu PG;Yin FX;Huan YH;Tomota Y;Nagai K .Texture dedicated grain size dependence of normal anisotropy in low-carbon steel strips[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1-2):8-17. |
| [5] | 关小军,周家娟,潘伟,朱学刚.Ti处理的ELC-BH钢板的析出物研究[J].钢铁,2002(07):50-53. |
| [6] | 吴雷,陈银莉,赵爱民,刘光明,熊爱明,薛俊平.冷轧压下率对390MPa级超低碳烘烤硬化钢组织性能和织构的影响[J].物理测试,2008(06):5-8,12. |
| [7] | 陈继平,康永林,郝英敏,刘光明.Ti+Nb超低碳烘烤硬化钢的组织和性能研究[J].热加工工艺,2009(06):13-16. |
| [8] | 王先进;关小军.超低碳烘烤硬化钢板的发展[J].国外钢铁,1993(05):41. |
| [9] | Warren P J;Cerezo A;Smith G D W .Observation of atomic planes in3DAP analysis[J].Ultramicroscopy,1998,73:261-266. |
| [10] | J.C. OH;T. OHKUBO;T. MUKAI .TEM and 3DAP Characterization of an Age-Hardened Mg-Ca-Zn Alloy[J].Scripta materialia,2005(6):675-679. |
| [11] | 王华,史文,何燕霖,符仁钰,李麟.Mn和P在超低碳烘烤硬化钢中的分布形态及其对拉伸行为的影响研究[J].金属学报,2011(03):263-268. |
| [12] | Chen T R;Hua M;Garcia C L.铌对冷轧退火高强无间隙原子铜中磷和锰偏聚行为的作用[J].超低碳钢,2006:327-335. |
| [13] | 戢景文;刘芬娣;王登京 等.汽车钢烘烤硬化性机理的内耗研究[J].金属学报,1999,35(09):913-919. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%