A new technique, powder compact foaming process for the production of aluminum foams has been studied in this article. According to this method, the aluminum powder is mixed with a powder foaming agent (TiH2). Subsequent to mixing, the powder blend is hot compacted to obtain a dense semi-finished product. Upon heating to temperatures within the range of the melting point, the foaming agent decomposes to evolve gas and the semi-finished product expands into a porous cellular aluminum. Foaming process is the key in this method. Based on experiments, the foaming characteristics were mainly analyzed and discussed. Experiments show that the aluminum-foam with closed pores and a uniform cell structure of high porosity can be obtained using this method by adjusting the foaming parameters: the content of foaming agent and foaming temperature.
参考文献
| [1] | G J Davies .[J].Journal of Materials Science,1983,18:1899. |
| [2] | J.Banhart .[J].Progress in Materials Science,2001,46:598. |
| [3] | J Baumeister;J Banhart;M Weber .[J].Materials & Design,1997,18:217. |
| [4] | H D Kunze;J Baumeister;J Banhart .[J].Practice and Management,1993,25(04):182. |
| [5] | Z T Wang .[J].Light Alloy Fabrication Technology,1999,27(11):1. |
| [6] | F Baumgrtner;L Duarte;J Banhart .[J].Advances in Engineering Materials,2000,2(04):168. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%