The nanocrystalline microstructure of the surface of 316 stainless steel (316SS) induced by surface me-chanical attrition treatment (SMAT) was determined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The technique of hydrogen embrittlement was first used to obtain the information of the brittleness cleavage plane. The effects of SMAT and the following annealing process on the corrosion behavior of 316SS were investiga-ted by potentiodynamic polarization curves and potentiostatic critical pitting temperature measurements. The results demonstrated that the nanocrystalline layer with an average grain size of 19 nm was produced. However, there were lots of cracks on the surface, which led to the degradation in the corrosion resistance of 316SS after SMAT. Never-theless, after annealing treatment, the corrosion resistance of the nanocrystalline surface had been improved greatly. The higher the annealing temperature, the better was the corrosion resistance.
参考文献
| [1] | WU Xiao-lei;TAO Nai-rong;HONG You-shi et al.Microstructure and Evolution of Mechanically-Induced Ultrafine Grain in Surface Layer of AI-AIIoy Subjected to USSP[J].Acta Materialia,2002,50(08):2075. |
| [2] | G. Liu;J. Lu;K. Lu .Surface nanocrystallization of 316L stainless steel induced by ultrasonic shot peening[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1):91-95. |
| [3] | N. R. Tao;Z. B. Wang;W. P. Tong;M. L. Sui;J. Lu;K. Lu .An investigation of surface nanocrystallization mechanism in Fe induced by surface mechanical attrition treatment[J].Acta materialia,2002(18):4603-4616. |
| [4] | H. W. Zhang;Z. K. Hei;G. Liu;J. Lu;K. Lu .Formation of nanostructured surface layer on AISI 304 stainless steel by means of surface mechanical attrition treatment[J].Acta materialia,2003(7):1871-1881. |
| [5] | Barbueci A;Farne G;Matteazzi P et al.Corrosion Behaviour of Nanoerystalline Cu9ONilO Alloy in Neutral Solution Containing Chlorides[J].Corrosion Science,1999,41(03):463. |
| [6] | V.A inogradov;T. Mimaki;S.Hashimoto;R.Valiev .On the corrosion behaviour of ultra-fine grain copper.[J].Scripta materialia,1999(3):319-326. |
| [7] | A. Balyanov;J. Kutnyakova;N. A. Amirkhanova;V. V. Stolyarov;R. Z. Valiev;X. Z. Liao;Y. H. Zhao;Y. B. Jiang;H. F. Xu;T. C. Lowe .Corrosion resistance of ultra fine-grained Ti[J].Scripta materialia,2004(3):225-229. |
| [8] | LU Ke;LU Jian .Nanostructured Surface Layer on Metallic Materials Induced by Surface Mechanical Attrition Treatment[J].Materials Science and Engineering,2004,375A-377A:38. |
| [9] | Klug H P;Alexander L E.X-Ray Diffraction Procedures for Polyerystalline and Amorphous Materials[M].New York:wiley,1974 |
| [10] | Cigada A;Mazza B;Pedeferri P et al.Stress Corrosion Cracking of Cold-Working Austenitic Stainless Steels[J].Corrosion Science,1982,22(06):558. |
| [11] | WANG Lin-chun;LI Dong-yang .Mechanical,Electrochemical and Tribological Properties of Nanocrystalline Surface of Brass Produced by Sandblasting and Annealing[J].Surface and Coatings Technology,2003,167(02):188. |
| [12] | Z. B. Wang;N. R. Tao;W. P. Tong;J. Lu;K. Lu .Diffusion of chromium in nanocrystalline iron produced by means of surface mechanical attrition treatment[J].Acta materialia,2003(14):4319-4329. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%