采用液相化学还原法,在水体系中,以醋酸铜为前驱体,坏抗血酸(Vc)为还原剂,引入微波辐照,加入适量自制表面活性剂为修饰剂,合成了长约90nm、直径为3nm的针形纳米铜.通过X射线衍射(XRD)、透射电子显微镜(TEM)和热重-差热分析(TG-DSC)对纳米铜进行了表征.将所制备的纳米铜添加到环氧树脂中并制成涂层,经数字导电仪检测,与添加球形纳米Cu的涂层相比,该涂层获得了优异的导电能力.前者pV=3.41×10-5Ω·m,后者ρV=8.9×10-5Ω·m.
参考文献
| [1] | Edelstein A S et al.[J].Progress in Materials Science,1997,42:5. |
| [2] | Wang H C et al.[J].Journal of Physical Chemistry B,2005,109:4309. |
| [3] | Andrievski R A;Glezer A M .[J].Sensors and Materials,2001,44:1621. |
| [4] | Rajeev S R et al.[J].Journal of Physical Chemistry B,2005,109:2086. |
| [5] | Shingo I et al.[J].Journal of Physical Chemistry B,2004,108:15599. |
| [6] | Zhang XF;Yin HB;Cheng XN;Jiang ZG;Zhao X;Wang AL .Modifying effects of polyethylene glycols and sodium dodecyl sulfate on synthesis of Ni nanocrystals in 1,2-propanediol[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(23):8067-8072. |
| [7] | Qin Y;Li H;Zhang Z K et al.[J].Organic Letters,2002,4(15):3123. |
| [8] | Joanna P C et al.[J].Journal of Physical Chemistry B,2001,105:2297. |
| [9] | Wu S H;Chen D H .[J].Journal of Colloid and Interface Science,2004,273:165. |
| [10] | Chen S W;Sommers J M .[J].Journal of Physical Chemistry B,2001,105:8816. |
| [11] | 张锡凤,殷恒波,程晓农,赵歆,蒋忠桂,王爱丽.修饰剂对液相还原法制备的纳米镍粒子形貌与尺寸的影响[J].金属学报,2006(04):383-388. |
| [12] | Zhang X F et al.[J].Materials Research Bulletin,2006,41:2041. |
| [13] | Cheng XN;Zhang XF;Yin HB;Wang AL;Xu YQ .Modifier effects on chemical reduction synthesis of nanostructured copper[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(5):2727-2732. |
| [14] | Braos G P;Mairellea T P;Rodriguez C E et al.[J].Journal of Molecular Catalysis A:Chemical,2003,193:185. |
| [15] | 何益艳,杜仕国.铜系复合涂料的制备及导电性能[J].化工新型材料,2004(06):49-51. |
| [16] | 闫军,崔海萍,杜仕国,施冬梅,鲁彦玲.环氧-铜粉体系导电涂料的制备工艺[J].材料保护,2003(10):30-31,36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%