研究了Cu-15Ni-15Ag合金在600～700℃空气中的氧化 .合金由富Ag的α相与Cu-Ni固溶体β相组成；氧化速率基本服从抛物线规律，合金的成膜速 率与纯Cu氧化近似.不同温度下合金均形成了最外层为CuO，内层为Cu2O，NiO以及Ag颗粒 组成的复杂氧化膜.在700℃氧化时观察到典型的Ni的内氧化，同时，由于Ni优先溶解于CuO 中影响了CuO-Cu2O氧压平衡，导致形成了CuO位于Cu2O下的特殊氧化膜结构.
The oxidation of Cu-15Ni-15Ag alloy in air has been studied at 600～700℃.The alloy contains a mixture of a silver-rich phase (α) w ith a phase mostly composed of a copper-nickel solid solution (β).Thus, the all oy is ternary two-phase systems containing two reactive metals with different af finity for oxygen plus a noble metal.The oxidation rate of the alloy under const ant temperature decreases generally with time and is only approximately paraboli c, showing some short periods of accelerated oxidation.The scaling rates of the alloy are substantially similar to those for the oxidation of pure copper, in sp ite of the presence of silver metal and of NiO in the scales.A region of interna l oxidation of nickel of the classical type is observed for oxidation at 700℃.A peculiar structure observed at 700℃is the presence of CuO beneath a Cu2O lay er, which is attributed to an effect of the preferential dissolution of nickel i n CuO on the oxygen pressure for the Cu2O-CuO equilibrium.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | |
| [13] | |
| [14] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%