采用Nd∶YAG激光进行了5A90铝锂合金3 mm厚薄板对接接头的激光焊接试验,采用电子背散射衍射(EBSD)技术对水平面和横截面焊缝组织的晶粒形态及晶粒取向进行了研究.结果表明,5A90铝锂合金激光焊缝金属在熔合线附近形成了非常狭窄的等轴非枝晶区(non-dendritic equiaxed grain zone,EQZ),在焊缝的其余区域形成了晶粒取向随机分布的等轴枝晶组织.由于焊缝熔合线附近EQZ的存在,焊缝金属晶粒没有继承母材晶粒的取向而外延生长,而是形成了一种非联生结晶生长的模式.焊缝区等轴枝晶的非均匀形核质点来源于平衡四方相β (Al3Zr)粒子,等轴枝晶的形态取决于固液相前沿较高的成分过冷,5A90铝锂合金的成分及激光焊接工艺特点促进了非均匀形核.
参考文献
| [1] | 巴瑞章;巩水利.[A].北京:机械工业出版社,2005:417. |
| [2] | 熊焕.低温贮箱及铝锂合金的应用[J].导弹与航天运载技术,2001(06):33-40,46. |
| [3] | 狄欧.铝锂合金的焊接技术研究进展[J].航空制造技术,2006(09):90-93. |
| [4] | Farai N;Chen D L;Zhou Y .[J].Journal of Alloys and Compounds,2011,509(03):982. |
| [5] | Wang H S;Chen H G;Jang J S C .[J].Journal of Alloys and Compounds,2010,495(01):224. |
| [6] | Zhao H;White D R;Debroy T .[J].International Materials Reviews,1999,44(06):238. |
| [7] | Molian A;Srivatsan T S .[J].Journal of Materials Science,1990,25(07):3347. |
| [8] | Kostrivas A D;Lippold J C .[J].JOM-Journal of the Minerals Metals and Materials Society,2004,56(02):65. |
| [9] | Gutierrez A E;Lippold J C .[J].Welding Journal,1998,77(03):123s. |
| [10] | Lin DC.;Wang GX.;Srivatsan TS. .A mechanism for the formation of equiaxed grains in welds of aluminum-lithium alloy 2090[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):304-309. |
| [11] | 于尔靖;郝传勇;应慧筠 et al.[J].焊接学报,1996,17(01):1. |
| [12] | 李小飞 .Study on the Solidification Cracking Susceptibility and Filler Metals for Welding of 2195Aluminum Lithium Alloys[D].北京:北京航空材料研究所,2007. |
| [13] | Sheikhi M;Malek Ghaini F;Torkamany M J et al.[J].Science and Technology of Welding and Joining,2009,14(02):161. |
| [14] | 杨平.电子背散射衍射技术及其应用[M].北京:冶金工业出版社,2007:65. |
| [15] | Kumar S;Mcshane H B;Sheppard T .[J].Materials Science and Technology,1994,10(02):162. |
| [16] | Hao C Y;Yu E J;Ying H Y et al.[J].Acta Metallurgica Sinica,1996,32(06):647. |
| [17] | Kou S.Welding Metallurgy (Second Edition)[M].USA:A John Wiley & Sons,Inc.,Publication,2003:145. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%