通过简单的液相沉淀法制备出棉絮状二氧化锰纳米颗粒,采用掺杂铁离子的方式对二氧化锰进行改性.热重曲线显示,掺杂Fe之后增加了产物中结合水的含量.由SEM可知,加入铁离子之后并没有改变二氧化锰的表面形貌,XRD与面扫结果表明铁离子以均一的方式掺杂到了二氧化锰中.循环伏安与恒电流充放电测试了材料的电化学性能,结果显示当掺杂量为2%时材料具有最好的电化学性能,担载量为3 mg·cm-2的情况下,放电比容量高达347.0 F·g-1,循环1000圈后容量的保持率为81.4%.
参考文献
[1] | Meiling Zhou;Hui Chai;Dianzeng Jia.The glucose-assisted synthesis of a graphene nanosheet-NiO composite for high-performance supercapacitors[J].New Journal of Chemistry,20146(6):2320-2326. |
[2] | Duay, J.;Sherrill, S.A.;Gui, Z.;Gillette, E.;Lee, S.B..Self-limiting electrodeposition of hierarchical MnO_2 and M(OH)_2/MnO_2 nanofibril/nanowires: Mechanism and supercapacitor properties[J].ACS nano,20132(2):1200-1214. |
[3] | 殷金玲;李一栋.导电聚合物复合材料作为超级电容器电极材料[J].化学工程师,2011(7):42-44,47. |
[4] | 田艳红;付旭涛;吴伯荣.超级电容器用多孔碳材料的研究进展[J].电源技术,2002(6):466-469,479. |
[5] | Ruiting Dong;Qinglan Ye;Lili Kuang.Enhanced Supercapacitor Performance of Mn3O4 Nanocrystals by Doping Transition-Metal Ions[J].ACS applied materials & interfaces,201319(19):9508-9516. |
[6] | 韩静香;佘利娟;翟立新;刘宝春.化学沉淀法制备纳米二氧化硅[J].硅酸盐通报,2010(3):681-685. |
[7] | 张孟;朱协彬;陈海清;孙坤;王舰;张垒.液相沉淀法制备的棒状α-MnO2研究[J].河南工程学院学报(自然科学版),2014(1):44-48. |
[8] | P. Ragupathy;Dae Hoon Park;Guy Campet.Remarkable Capacity Retention of Nanostructured Manganese Oxide upon Cycling as an Electrode Material for Supercapacitor[J].The journal of physical chemistry, C. Nanomaterials and interfaces,200915(15):6303-6309. |
[9] | Zheng JP.;Jow TR.;Cygan PJ..HYDROUS RUTHENIUM OXIDE AS AN ELECTRODE MATERIAL FOR ELECTROCHEMICAL CAPACITORS[J].Journal of the Electrochemical Society,19958(8):2699-2703. |
[10] | Kanoh H.;Makita Y.;Ooi K.;Tang WP..ELECTROCHEMICAL INTERCALATION OF ALKALI-METAL IONS INTO BIRNESSITE-TYPE MANGANESE OXIDE IN AQUEOUS SOLUTION[J].Langmuir: The ACS Journal of Surfaces and Colloids,199725(25):6845-6849. |
[11] | Athouel L;Moser F;Dugas R;Crosnier O;Belanger D;Brousse T.Variation of the MnO2 birnessite structure upon charge/discharge in an electrochemical supercapacitor electrode in aqueous Na2SO4 electrolyte[J].The journal of physical chemistry, C. Nanomaterials and interfaces,200818(18):7270-7277. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%