通过溶液沉淀法制备了二氧化钛交联的三元乙丙橡胶(EPDM)复合材料,扫描电镜和溶解、溶胀结果表明二氧化钛有效地交联了EPDM基体,全反射傅立叶红外光谱表明偶联剂修饰二氧化钛颗粒和EPDM接枝马来酸酐是有效交联的重要原因.随着二氧化钛填充量的增加,使基本无力学性能的三元乙丙橡胶力学强度提高到6.2 MPa,断裂伸长率提高到2435%,热分解温度提高20℃,进一步增加填充量,由于粒子之间的聚集而使复合材料性能下降.
参考文献
| [1] | Liu X.;Huang H.;Xie ZY.;Zhang Y.;Zhang YX.;Sun K.;Min LN. .EPDM/polyamide TPV compatibilized by chlorinated polyethylene[J].Polymer Testing,2003(1):9-16. |
| [2] | Huang H.;Yang JL.;Liu X.;Zhang YX. .Dynamically vulcanized ethylene propylene diene terpolymer/nylon thermoplastic elastomers[J].European Polymer Journal,2002(5):857-861. |
| [3] | Siriwardena S.;Ishiaku US.;Ismail H. .Effect of mixing sequence in the preparation of white rice husk ash filled polypropylene/ethylene-propylene-diene monomer blend[J].Polymer Testing,2001(1):105-113. |
| [4] | Gwaily SE.;Madani M.;Abdel-Aziz MM. .Thermal and electrical studies on irradiated silica-ethylene-propylene diene monomer (SiO2/EPDM) composites[J].Polymer Testing,1998(4):265-287. |
| [5] | 朱雨涛,高乃奎,王新珩,谢恒堃.含填料聚合物（EPDM）的松弛过程[J].高分子材料科学与工程,1998(03):97-99. |
| [6] | Zhang J;Ding QJ;Hu BX;Liu BL;Shen J .Preparation and characterization of composites: Ethylene-propylene-diene terpolymer-graft-maleic anhydride/CaCO3[J].Journal of Applied Polymer Science,2006(3):1810-1815. |
| [7] | 李伟,黄玉东,陈平.熔体插层法制备EPDM/蒙脱土纳米复合材料[J].高分子材料科学与工程,2008(02):136-139. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%