采用溶胶-凝胶法,以乙烯基三乙氧基硅烷(KH151)和正硅酸乙酯(TEOS)为前驱体、用浸渍提拉法在工业铝管表面制备了硅氧膜.通过金相显微镜观察了硅氧膜的表面形貌,通过硫酸铜点滴、盐雾试验、析氢实验和Tafel曲线、交流阻抗谱(EIS)等电化学方法对铝管表面硅氧膜的耐蚀性能进行了考察.结果表明,硅氧膜均匀、致密、平整,它使铝管的自腐蚀电位明显正移;相对于空白试样,铬钝化铝管和涂有硅氧膜的铝管的自腐蚀电流密度分别下降了1和2个数量级,硅氧膜电极体系总电阻是空白试样总电阻的6.1倍、是铬钝化膜总电阻的1.48倍.
参考文献
| [1] | 沈学明.家用电冰箱铝蒸发器内漏成因及对策[J].制冷与空调,2002(04):70-72. |
| [2] | 梁永煌,满瑞林.Al管表面有机杂化膜的制备及性能表征[J].金属学报,2010(12):1522-1528. |
| [3] | 周渝生.无铬钝化技术研究的进展[J].钢铁,2003(04):68-71. |
| [4] | 王文忠.铝及其合金化学转化膜处理[J].电镀与环保,2002(06):24-25. |
| [5] | A.N. Khramov;N.N. Voevodin;V.N. Balbyshev;R.A. Mantz .Sol-gel-derived corrosion-protective coatings with controllable release of incorporated organic corrosion inhibitors[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2005(1/2):191-196. |
| [6] | Z. Feng;Y. Liu;G. E. Thompson;P. Skeleton .Sol-gel coatings for corrosion protection of 1050 aluminium alloy[J].Electrochimica Acta,2010(10):3518-3527. |
| [7] | Wang, D;Bierwagen, GR .Sol-gel coatings on metals for corrosion protection[J].Progress in Organic Coatings,2009(4):327-338. |
| [8] | 王云芳.溶胶-凝胶法制备γ-缩水甘油醚丙基三甲氧基硅烷/正硅酸乙酯杂化材料研究[J].应用化工,2006(10):795-797. |
| [9] | 李凌杰,欧孝通,陈德贤,张元,雷惊雷,张胜涛.改进溶胶-凝胶工艺制备铝合金硅基防护膜[J].腐蚀科学与防护技术,2009(02):197-199. |
| [10] | 郭增昌,王云芳,王汝敏,熊艳丽.铝合金表面防腐蚀处理新工艺[J].材料保护,2005(04):25-27. |
| [11] | 刘琰,尤宏,胡立江,张小明,孙德智.VMS有机-无机杂化膜的制备及其防腐性能研究[J].哈尔滨工业大学学报,2005(10):1344-1347. |
| [12] | 李鑫庆;陈迪勤;余静琴.化学转化膜技术与应用[M].北京:机械工业出版社,2005:157-176. |
| [13] | 刘倞,胡吉明,张鉴清,曹楚南.金属表面硅烷化防护处理及其研究现状[J].中国腐蚀与防护学报,2006(01):59-64. |
| [14] | 幸松民;王一璐.有机硅合成工艺及产品应用[M].北京:化学工业出版社,2000:125-138. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%