采用多弧离子镀技术在4Cr13不锈钢上沉积TiN薄膜,在其他参数不变的条件下,研究不同弧电流下薄膜的组织、结构及性能.利用扫描电子显微镜、X射线衍射仪、显微硬度计、划痕仪和往复式摩擦磨损仪分别对薄膜进行表面形貌观察,物相分析,以及表面硬度、结合力、耐磨性检测.实验结果表明:孤电流对薄膜的表面形貌有明显的影响,随着弧电流的增大,薄膜表面的液滴数目和尺寸逐步增大;薄膜的相结构主要由TiN相组成,在(111)面有较强的择优取向,且随着弧电流的增大,衍射峰强度略有增加;随着孤电流的增大,薄膜的硬度先增大后减小,硬度值最大为2897HV;随着弧电流的增大,薄膜的结合力先增大后减小,当弧电流为105 A时,薄膜的结合力最大,为75 N;随着弧电流的增大,薄膜的摩擦系数先减小后增大,当弧电流为105 A时,薄膜的耐磨性最好.
参考文献
| [1] | Musil J;Vlcek J .A perspective of magnetron sputtering in surface engineering[J].Surface and Coatings Technology,1999,112(1-3):162. |
| [2] | Subramanian B;Ashok K;Jayachandran M .Effect of substrate temperature on the structural properties of magnetron sputtered titanium nitride thin films with brush plated nickel interlayer on mild steel[J].Applied Surface Sinence,2008,255(5):2133. |
| [3] | Benegra M;Lamas DG;de Rapp MEF;Mingolo N;Kunrath AO;Souza RM .Residual stresses in titanium nitride thin films deposited by direct current and pulsed direct current unbalanced magnetron sputtering[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(1/2):146-150. |
| [4] | 史新伟,邱万奇,刘正义.电弧离子镀TiN薄膜中的缺陷及其形成原因[J].中国表面工程,2006(01):43-46. |
| [5] | 孙伟,宫秀敏,叶卫平,张覃铁,朱小清.三种材料多弧离子镀TiN涂层性能比较[J].电加工与模具,2000(01):31-33. |
| [6] | 姜雪峰,刘清才,王海波.多弧离子镀技术及其应用[J].重庆大学学报（自然科学版）,2006(10):55-57,68. |
| [7] | 刘海 .电弧离子镀氮化铬涂层的组织结构及性能研究[D].长春:吉林大学,2006. |
| [8] | Boxman R L;Goldsmith S S .The interaction between plasma and macroparticles in a multi-cathode-spot vacuum arc[J].Journal of Applied Physics,1981,52(1):151. |
| [9] | Mattews A;Lefkow A R .Problems in the physical vapour deposition of titanium nitride[J].THIN SOLID FILMS,1984,126(3-4):283. |
| [10] | Pang Z;Boumerzoug M;Kruzelecky R V et al.Low temperature radio frequency sputter deposition of TiN films using optical emission spectroscopy sa process monitor[J].J Vac Sci Techn A,1994,12(1):83. |
| [11] | 孙伟,宫秀敏,叶卫平,张覃铁,朱小清.多弧离子镀TiN涂层结合力的影响因素[J].材料保护,2000(08):31-32. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%