利用溶胶-凝胶法制备超细氢氧化锆颗粒并用BET比表面积测试,系统地研究了超声分散、陈化条件、干燥温度、反应温度等制备条件对氢氧化锆活性的影响.利用TEM、HRTEM对所制得的氢氧化锆样品进行表征.试验表明:采用溶胶-凝胶法可以制得直径为10nm左右的氢氧化锆颗粒,颗粒由厚度约为1nm、直径约为4nm的片状分子堆积构成.制备比表面积较高的氢氧化锆样品的最佳工艺参数:反应温度为60℃,超声振荡周期为1∶3,超声分散的时间为15min,陈化温度为60℃,陈化时间为30min,干燥温度为100℃.
参考文献
| [1] | Peter D Southon;John R Bartlett et al.Formation and characterization of an aqueous zirconium hydroxide colloid[J].Chemistry of Materials,2002,14:4313. |
| [2] | Guo Gongyi;Chen Yuli et al.Thermal,spectroscopic and X-ray diffractional analyses of zirconium hydroxides precipitated at low pH values[J].Materials Chemistry and Physics,2004,84:308. |
| [3] | Dan Frcasiu;Li Jingqi .Preparation of sulfated zirconia catalysts with improved control of sulfur content,III.Effect of conditions of catalyst synthesis on physical properties and catalytic activity[J].Applied Catalysis A:General,1998,175(01) |
| [4] | Toshishige M. Suzuki;John O. Bomani;Hideyuki Mastunaga .Preparation of porous resin loaded with crystalline hydrous zirconium oxide and its application to the removal of arsenic[J].Reactive & functional polymers,2000(1/2FEBRUAYR):165-172. |
| [5] | 刘红研,徐学峰,朱建华.吸附法脱除卤水中SO2-4的试验研究[J].石油大学学报(自然科学版),2002(06):102-104. |
| [6] | 志贺稔.脱除硫酸根的新方法(NDS法)[J].氯碱工业,1993(07):8. |
| [7] | 韩利成;唐南龙 等.均匀分散氢氢化锆胶体的制备[J].硅酸盐通报,1990,9(04):16. |
| [8] | 葛荣德;刘志宏 等.工艺条件对氢氧化锆凝胶性能的影响[J].中南工业大学学报(自然科学版),1995,26(01):52. |
| [9] | 赵青,常爱民,简家文,巴维真.改性溶胶-凝胶法制备ZrO2纳米晶粉及其团聚控制[J].中国粉体技术,2003(05):14-17. |
| [10] | 于庆杰,王祥彬.超声波在超细粉体分散中的应用[J].聚酯工业,2004(03):30-31. |
| [11] | 张喜梅,陈玲,李琳,郭祀远.超声场对水合氧化锆胶体制备的影响[J].声学技术,2003(02):117-119,135. |
| [12] | 酒金婷,葛钥,张涑戎,李立平,屠凡,朱鹤孙.无团聚纳米氧化锆的制备及应用[J].无机材料学报,2001(05):867-871. |
| [13] | 栾伟玲;高濂 等.纳米粉体干燥方法的研究[J].无机材料学报,1997,12(06):835. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%