为了改善聚醚型聚氨酯弹性体(PU)的力学性能,运用互穿聚合物网络(IPN)技术,分别将端正己烷基、端十二烷基、端十八烷基超支化聚酯(HBP-C6、HBP-C12、HBP-C18)引入至PU中形成共混体系.结果表明,相比于空白胶片,PU/HBP IPN体系的力学性能有了一定的提高,超支化聚酯端烷烃链越长,相畴尺寸逐渐减小,互穿程度更高;高含量的HBP-C18加入后,随着其质量分数的增加,互穿网络胶片的拉伸强度和断裂伸长率均呈现出先增大后减小的趋势,加入30％的HBP-C18时,形成了双相连续的微观结构;采用“准一步法”和“一步法”合成端十八烷基超支化聚酯,分别与聚氨酯形成互穿网络,力学测试结果表明,前者的力学性能优于后者.
参考文献
| [1] | LEE DA-KONG;TSAI HONG-BING .Properties of Segmented Polyurethanes Derived from Different Diisocyanates[J].Journal of Applied Polymer Science,2000(1):167-174. |
| [2] | Saha, MC;Kabir, ME;Jeelani, S .Enhancement in thermal and mechanical properties of polyurethane foam infused with nanoparticles[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):213-222. |
| [3] | C.Gao;D.Yan .Hyperbranched polymers:from synthesis to applications[J].Progress in Polymer Science,2004(3):183-275. |
| [4] | Zhang J;Hu CP .Synthesis, characterization and mechanical properties of polyester-based aliphatic polyurethane elastomers containing hyperbranched polyester segments[J].European Polymer Journal,2008(11):3708-3714. |
| [5] | 宋雪晶,罗运军,李国平,柴春鹏.超支化聚醚/丁羟聚氨酯互穿网络的制备及力学性能[J].高分子材料科学与工程,2009(03):1-4. |
| [6] | 巢玲玲,刘晶如,俞强.端羟基改性超支化聚酯的热稳定性及分解行为[J].现代塑料加工应用,2012(01):12-15. |
| [7] | 刘晶如,张建勋,巢玲玲,俞强.端基对脂肪族超支化聚酯性能的影响[J].高校化学工程学报,2011(06):1051-1056. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%