By means of dynamic plastic deformation (DPD) followed by thermal annealing, a mixed structure of microsized austenite grains embedded with nano-scale twin bundles (of about 20% in volume) has been synthesized in a 316L stainless steel (SS). Such a 316L SS sample exhibits a tensile strength as high as 1001 MPa and an elongation-to-failure of about 23%. The much elevated strength originates from the presence of a considerable number of strengthening nano-twin bundles, while the ductility from the recrystallized grains. The superior strength-ductility combination achieved in the nano-twins-strengthened austenite steel demonstrates a novel approach for optimizing the mechanical properties in engineering materials.

参考文献

[1] B.P. Kashyap .Towards interrelationship of grain size, cell parameters and flow stress in type 316L stainless steel[J].Acta materialia,2002(9):2413-2427.
[2] A.Kumar;T.Jayakumar;P.Palanichamy;B.Raj .Influence of grain size on ultrasonic spectral parameters in AISI type 316 stainless steel[J].Scripta materialia,1999(3):333-340.
[3] X.H. CHEN;J. LU;L. LU .Tensile properties of a nanocrystalline 316L austenitic stainless steel[J].Scripta materialia,2005(10):1039-1044.
[4] Y.S. Li;N.R. Tao;K. Lu .Microstructural evolution and nanostructure formation in copper during dynamic plastic deformation at cryogenic temperatures[J].Acta Materialia,2008(2):230-241.
[5] M. Eskandari;A. Najafizadeh;A. Kermanpur .Effect of strain-induced martensite on the formation of nanocrystalline 316Lstainless steel after cold rolling and annealing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):46-50.
[6] Y.S. Li;Y. Zhang;N.R. Tao .Effect of thermal annealing on mechanical properties of a nanostructured copper prepared by means of dynamic plastic deformation[J].Scripta materialia,2008(4):475-478.
[7] Z.-H. Jin;P. Gumbsch;K. Albe .Interactions between non-screw lattice dislocations and coherent twin boundaries in face-centered cubic metals[J].Acta materialia,2008(5):1126-1135.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%