对C/SiC复合材料表面SiC涂层在1300℃干氧和湿氧环境中退火处理60 h,利用显微CT技术对高温氧化后的SiC涂层进行无损检测。通过重构SiC涂层不同深度的氧化形貌,并利用SEM、EDS和XRD进行辅助验证,得到沿SiC涂层表面和厚度方向的氧化形貌。结果表明：显微CT能有效地检测氧化后SiC涂层中存在的氧化产物SiO2及其氧化深度,其在表面及深度方向均呈非均匀分布;在干氧环境中SiC涂层的氧化面积沿着涂层的深度方向呈减少趋势,而在湿氧环境中SiC涂层的氧化面积沿着涂层的深度方向呈先增加后递减的趋势,验证了C/SiC复合材料表面SiC涂层在干氧和湿氧中不同的氧化机制。
The SiC coatings on the surface of C/SiC composites which were annealed in the dry and wet oxidizing environment at 1300 ℃ for 60 h were examined nondestructively using X-ray microtomography（Micro CT）.The oxidation morphology along the coating surface and depth direction was investigated by reconstructing images of different depth SiC coatings assisted with SEM,EDS and XRD.The results demonstrate that Micro CT is applicable to distinguish the oxidation products of SiO2 in the SiC coating and the oxidation depth.Oxidation products SiO2 along the SiC coating surface and depth direction is non-uniform distribution.With increasing depth of the coating,the oxidized area percentage of the coating decreases in the dry oxidizing environment;and first increases and then decreases in the wet oxidizing environment.The different oxidation mechanisms of SiC coatings in the dry and wet oxidizing environment are confirmed by Micro CT.
参考文献
| [1] | Ohnabe H, Masaki S, Onozuka M, et al. Potential application of ceramic matrix composites to aero-engine components [J]. Composites Part A: Applied Science and Manufacturing, 1999, 30(4): 489-496. |
| [2] | 张立同, 成来飞, 徐永东. 新型碳化硅陶瓷基复合材料的研究进展[J]. 航空制造技术, 2003(1): 23-32. |
| [3] | Yin X W, Cheng L F, Zhang L T, et al. Oxidation behavior of 3D C/SiC composites in two oxidizing environments [J]. Composites Science and Technology, 2001, 61(7): 977-980. |
| [4] | Cheng L F, Xu Y D, Zhang L T, et al. Oxidation behavior from room temperature to 1500 ℃ of 3D C/SiC composites with different coatings [J]. Journal of the American Ceramic Society, 2002, 85(4): 989-991. |
| [5] | Wu S J, Cheng L F, Yang W B, et al. Oxidation protective multilayer CVD SiC coatings modified by a graphitic B-C interlayer for 3D C/SiC composite [J]. Applied Composite Materials, 2006, 13(6): 397-406. |
| [6] | Zhang Y, Zhang L T, Cheng L F, et al. Stress-oxidation behavior of a carbon/silicon carbide composite in a high-temperature combustion environment [J]. Journal of the American Ceramic Society, 2008, 91(1): 291-295. |
| [7] | Zhang Q, Lee P D, Singh R, et al. Micro-CT characterization of structural features and deformation behavior of flyash/aluminum syntactic foam [J]. Acta Materialia, 2009, 57(10): 3003-3011. |
| [8] | Weber E, Fernandez M, Wapner P, et al. Comparison of X-ray micro-tomography measurements of densities and porosity principally to values measured by mercury porosimetry for carbon-carbon composites [J]. Carbon, 2010, 48(8): 2151-2158. |
| [9] | 孙磊, 张立同, 梅辉, 等. 2D C/SiC缺陷的无损检测与评价[J]. 复合材料学报, 2008, 25(5): 85-90. |
| [10] | 邓晓东, 成来飞, 梅辉, 等. C/SiC复合材料的定量红外波无损检测[J]. 复合材料学报, 2009, 26(5): 112-119. |
| [11] | 刘红林, 金志浩, 郝志彪, 等. ICT 技术测试炭/炭复合材料内部密度分布[J]. 无损检测, 2007, 29(12): 726-728. |
| [12] | 曹玉玲, 孙玲霞. 工业CT在复合材料孔隙率分析中的应用[J]. CT理论与应用研究, 2001, 10(4): 14-17. |
| [13] | Stock S R. X-ray microtomography of materials [J]. International Materials Reviews, 1999, 44(4): 141-164. |
| [14] | Stock S R. Recent advances in X-ray microtomography applied to materials [J]. International Materials Reviews, 2008, 53(3): 129-181. |
| [15] | Schilling P J, Karedla B P R, Tatiparthi A K, et al. X-ray computed microtomography of internal damage in fiber reinforced polymer matrix composites [J]. Composites Science and Technology, 2005, 65(14): 2071-2078. |
| [16] | Schell J S U, Renggli M, van Lenthe G H, et al. Micro-computed tomography determination of glass fibre reinforced polymer meso-structure [J]. Composites Science and Technology, 2006, 66(13): 2016-2022. |
| [17] | Diukic L P, Herszberg I, Walsh W R, et al. Contrast enhancement in visualisation of woven composite tow architecture using a Micro-CT scanner, Part 1: Fabric coating and resin additives [J]. Composites Part A: Applied Science and Manufacturing, 2009, 40(5): 553-565. |
| [18] | 阚晋, 孟松鹤, 王军. C/C复合材料微观结构的CT分析[J]. 硅酸盐通报, 2006, 26(3): 198-200. |
| [19] | Quemard L, Rebillat F, Guette A, et al. Degradation mechanisms of a SiC fiber reinforced self-sealing matrix composite in simulated combustor environments [J]. Journal of the European Ceramic Society, 2007, 27(1): 377-388. |
| [20] | Opila E J, Hann Jr R E. Paralinear oxidation of CVD SiC in water vapor [J]. Journal of the European Ceramic Society, 1997, 80(1): 197-205. |
| [21] | Opila E J. Oxidation and volatilisation of silica formers in water vapor [J]. Journal of the American Ceramic Society, 2003, 86(8): 1238-1248. |
| [22] | Opila E J. Oxidation kinetics of chemically vapor-deposited silicon carbide in wet oxygen [J]. Journal of the American Ceramic Society, 1994, 77(3): 730-736. |
| [23] | Opila E J, Fox D S, Jacobson N S. Mass spectrometric identification of Si-O-H(g) species from the reaction of silica with water vapor at atmospheric pressure [J]. Journal of the American Ceramic Society, 1997, 73(12): 1009-1012. |
| [24] | Witte F, Fischer J, Beckmann F, et al. Three-dimensional microstructural analysis of Mg-Al-Zn alloys by synchrontron-radiation-based microtomography [J]. Scripta Materialia, 2008, 58(6): 453-456. |
| [25] | Amanat N, Tsafnat N, Bob C E, et al. Metallurgical coke an investigation into compression properties and microstructure using X-ray tomography [J]. Scripta Materialia, 2009, 60(2): 92-95. |
| [26] | 敖波, 张小海, 李春阳, 等. 疲劳裂纹扩展高分辨率CT分析新进展[J]. CT理论与应用研究, 2010, 19(2): 35-41. |
| [27] | 梅辉. 2D C/SiC在复杂耦合环境中的损伤演变和失效机制[D]. 西安: 西北工业大学, 2007: 91-93. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%