304 stainless steel coating was deposited on the IF steel substrate by cold gas dynamic spraying （CGDS）, and the elastic modulus of the 304 stainless steel coating was studied. The elastic modulus of cold sprayed 304 stain- less steel coating was measured using the three-point bend testing and the compound beam theory, and the other me- chanic parameters （such as the equivalent flexural rigidity and the moment of inertia of area） of the coatings were also calculated using this compound beam theory. It is found that the calculated results using the above methods are accu- rate and reliable. The elastic modulus value of the cold sprayed 304 stainless steel coating is 1. 179 X 105 MPa, and it is slightly lower than the 304 stainless steel plate （about 2 X 105 MPa）. It indicates that the elastic modulus of the cold sprayed coatings was quite different from the comparable bulk materials. The main reason is that the pores and other defects are existed in the coatings, and the elastic modulus of the coatings also depends on varies parameters such as the feed stock particle size, porosity, and processing parameters.
参考文献
| [1] | Sudharshan Phani Pardhasaradhi;Vishnukanthan Venkatachalapathy;Shrikant V. Joshi;Sundararajan Govindan .Optical Diagnostics Study of Gas Particle Transport Phenomena in Cold Gas Dynamic Spraying and Comparison with Model Predictions[J].Journal of Thermal Spray Technology,2008(4):551-563. |
| [2] | Spencer, K;Zhang, MX .The use of kinetic metallization to form intermetallic reinforced composite coatings by post-spray heat treatment[J].Surface & Coatings Technology,2009(20/21):3019-3025. |
| [3] | Novoselova T;Fox P;Morgan R;O'Neill W .Experimental study of titanium/aluminium deposits produced by cold gas dynamic spray[J].Surface & Coatings Technology,2006(8):2775-2783. |
| [4] | Lee H;Lee S;Shin H et al.Mechanical Matching and Micro- structural Evolution at the Coating/Substrate Interfaces of Cold Sprayed Ni,A1 Coatings[J].Journal of Alloys and Com- pounds,2009,478(1/2):636. |
| [5] | Wang H T;Li C J;Yang G J et al.Cold Spraying of Fe/A1 Powder Mixture:Coating Characteristics and Influence of Heat Treatment on the Phase Structure[J].Applied Surface Sci- ence,2008,255(05):2538. |
| [6] | Lee HY;Jung SH;Lee SY;You YH;Ko KH .Correlation between Al2O3 particles and interface of Al-Al2O3 coatings by cold spray[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(5):1891-1898. |
| [7] | Wu JW;Yang JG;Fang HY;Yoon S;Lee C .The bond strength of Al-Si coating on mild steel by kinetic spraying deposition[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(22):7809-7814. |
| [8] | Xueping Guo;Ga Zhang;Wenya Li;Yang Gao;Hanlin Liao;Christian Coddet .Investigation Of The Microstructure And Tribological Behavior Of Cold-sprayed Tin-bronze-based Composite Coatings[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2009(6):3822-3828. |
| [9] | Zhao ZB;Gillispie BA;Smith JR .Coating deposition by the kinetic spray process[J].Surface & Coatings Technology,2006(16/17):4746-4754. |
| [10] | Li CH;Li WY;Wang YY .Formation of metastable phases in cold-sprayed soft metallic deposit[J].Surface & Coatings Technology,2005(1/3):469-473. |
| [11] | Li CJ.;Li WY. .Deposition characteristics of titanium coating in cold spraying[J].Surface & Coatings Technology,2003(2/3):278-283. |
| [12] | Ajdelsztajn L;Zuniga A;Jodoin B;Lavernia EJ .Cold gas dynamic spraying of a high temperature Al alloy[J].Surface & Coatings Technology,2006(6):2109-2116. |
| [13] | Lima RS.;Karthikeyan J.;Kay CM.;Lindemann J.;Berndt CC. .Microstructural characteristics of cold-sprayed nanostructured WC-Co coatings[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2002(1/2):129-135. |
| [14] | Kim HJ;Lee CH;Hwang SY .Fabrication of WC-Co coatings by cold spray deposition[J].Surface & Coatings Technology,2005(2/3):335-340. |
| [15] | Kim H J;Lee C H;Hwang S Y .Superhard Nano WC-12%Co Coating by Cold Spray Deposition[J].Materials Science and Engineering A,2005,391(1/2):243. |
| [16] | Lee HY;Jung SH;Lee SY;Ko KH .Alloying of cold-sprayed Al-Ni composite coatings by post-annealing[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(7):3496-3502. |
| [17] | Stoloff N S;Liu C T;Deevi S C .Emerging Applications of Intermetallics[J].Intermetallics,2000,8(9/10/11):1313. |
| [18] | Hodge A M;Dunand D C .Synthesis of Niekel-Aluminide Foams by Pack-Aluminization of nickel Foams[J].Interme- tallies,2001,9(07):581. |
| [19] | T.E. Mitchell;J.P. Hirth;A. Misra .Apparent activation energy and stress exponent in materials with a high Peierls stress[J].Acta materialia,2002(5):1087-1093. |
| [20] | Hyung-Jun Kim;Young-Gak Kweon .Elastic modulus of plasma-sprayed coatings determined by indentation and bend tests[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1999(12):201-206. |
| [21] | Li JF.;Ding CX. .Determining microhardness and elastic modulus of plasma-sprayed Cr3C2-NiCr coatings using Knoop indentation testing[J].Surface & Coatings Technology,2001(2/3):229-237. |
| [22] | 程应科,张建军,徐连勇.涂层弹性模量的测量方法[J].中国科技论文在线,2008(04):293-298. |
| [23] | Bansal P;Shipway P H;Leen S B et al.Experimental Vali dation of FE Predicted Fracture Behaviour of Thermally Sprayed Coatings[J].Materials Science and Engineering A,2006,430(1/2):104. |
| [24] | Kai Zhang;Kun Zhang;Huai Xue Li;Guang Nan Chen .Interface fracture behavior of electroplated coating on metal substrate under compressive strain[J].Journal of Materials Processing Technology,2009(3):1337-1341. |
| [25] | 徐连勇,荆洪阳,霍立兴,张玉凤,马崇.高速电弧喷涂层的弹性模量[J].焊接学报,2005(04):13-15,20. |
| [26] | Sekiya S;Kakumakoto N;Tanimura S.The Latest Me- chanics of Materials[M].Tokyo Japan,1990 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%