发现了ZnO压敏陶瓷中的锥状或柱状“突起物”现象.通过能谱发现“突起物”的物质构成是ZnO,而且是ZnO晶粒生长形成的实体,并非气体在ZnO中形成的气泡.进一步论证了这种现象是ZnO极性生长造成的,并从内因和外因两个方面进行了分析.内因是ZnO的极性晶格结构和结晶形态,外因是ZnO压敏陶瓷中Bi2O3液相提供了极性生长得以显现的物化环境,并且通过单独添加Bi2O3的97mol%ZnO+3mol%Bi2O3配方和100mol%纯ZnO配方制备样品进行对比实验,验证了Bi2O3的作用.
The protuberance phenomenon in shape of conic or cylinder was discovered for the first time. It was found by EDS that the protuberance is entity formed by ZnO, not the air bubble. And it was proved that the polar growth of ZnO leads to the protuberance phenomenon. The detailed reasons were probed from internal and external courses. The internal course is the polar structure and morphology of ZnO crystal. The external course is the physical and chemical environment made by Bi2O3 liquid phase, and this conclusion was proved by the comparisons of the samples which fabricated by 97mol%ZnO+3mol%Bi2O3 (in mole) compound and 100mol% (in mole) ZnO compound.
参考文献
| [1] | Gupta T K. J. Am. Ceram. Soc., 1990, 73 (7): 1817-1840. [2] Mantas P Q, Baptista J L. J. Euro. Ceram. Soc., 1995, 15 (1): 605-615. [3] 仲维卓, 华素坤. 晶体生长形态学. 北京: 科学出版社, 1999. 336-352. [4] Hartman P, Perdok W G. Acta Cryst., 1955, 32 (8): 525. [5] Laudise R A. The Growth of Single Crystals. New Jersey: Prentice-Hall Inc, 1970. 293. [6] 张克从, 张乐潓. 晶体生长科学与技术. 北京: 科学出版社, 1997. 126. [7] Laudise R A, Kolb E D, Caporaso A J. J. Am. Cerm. Soc., 1964, 47 (1): 9. [8] 元如林, 施尔畏. 中国科学(E), 1997, 27 (3): ?29. [9] 仲维卓, 于锡玲, 罗豪素, 等. 中国科学(E), 1998, 28 (4): 320. [10] Sun X L, Brillson L J, Chiang Y M, et al. J. Appl. Phys., 2002, 92 (9): 5072-5076. [11] 莫以豪, 李标荣. 半导体陶瓷及其敏感元件. 上海: 上海科学技术出版?社, 1982. 120-176. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%