Surface modification of sericite by wet method was conducted with the addition of 1.0% (w/w) silane. The resulting wetting contact angle and activity ratio of sericite were 130° and 98% respectively.Good pre-evaluation indexes of oil value (40.8%) and dispersivity (14.0 mL) were obtained. When 30% of sericite was filled into acrylonitrile butadiene styrene(ABS) plastic, the bending strength and tensile strength of the composite material were reduced by 7% and 14.3% in comparison to those of pure ABS plastic, while the rigidity was increased by 3 times, and the impact strength and breaking elongation were reduced significantly.The mechanism of surface modification was investigated and the configuration of silane coupling agent on the surface of sericite was given. Infrared (IR) spectroscopic analysis indicates that the adsorption of silane on the surface of sericite belongs to chemical adsorption.
参考文献
| [1] | F G Sun;H F Zhang;Y K Ning.Speciality and Application of the Sericite[J].World Journal of Gastroenterology,2002(02):192-198. |
| [2] | 张敬阳,吴季怀,赵煌,吴伟端.绢云母表面改性的实验研究[J].矿物学报,2004(04):351-354. |
| [3] | Hokkaido.Surface Modification[A].London:Butterworths,1994:453-457. |
| [4] | Galembeck Fernando.Surface and Colloid Science[M].Berlin:Springer Publication,2004 |
| [5] | S L Zheng.Surface Modification of the Powder[M].北京:中国建筑工业出版社,1995 |
| [6] | 胡萍,姜明,黄畴,于谦.硅烷偶联剂的界面性能研究[J].表面技术,2004(05):19-21. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%