把Mg（OH）2 （Magnesium hydroxide, MH） 在不同温度热处理不同时间, 得到一系列不同热分解状态的Mg（OH）2 （Treated magnesium hydroxide, t-MH）。以MH和t-MH为无卤阻燃剂, 聚苯乙烯（PS）为基体, 采用熔体共混法制备了MH/PS和t-MH/PS复合材料。详细研究了MH热处理对t-MH/PS复合材料燃烧性能的影响, 并以此实验结果为基础提出了复合材料的阻燃机制模型。结果表明, 随着热处理温度升高、热处理时间延长, MH逐渐分解并转化成MgO。在相同条件下t-MH/PS复合材料的阻燃性能较MH/PS复合材料显著降低, 但是仍然比纯PS有明显提高。此外, MH热分解产生的MgO有促进PS成炭的作用。MH/PS复合材料的阻燃机制是以下几种因素协同作用的结果： （1）MH分解吸热的冷却降温作用;（2）MH热分解释放水蒸气的气相稀释作用;（3）MH热分解产物MgO的固相阻隔与防护作用;（4）MgO促进PS成炭阻燃作用。
A series of Mg(OH)2 with different degradation states (t-MH) were obtained by pyrolyzing Mg(OH)2 (Magnesium hydroxide, MH) at various temperatures for different time. MH/PS and t-MH/PS composites were prepared by melt-compounding MH and t-MH as halogen-free flame retardants and PS as matrix. The influence of thermal treatment of MH on combustion behavior of t-MH/PS composites was investigated in detail. Based on the experimental results, a model of the flame retardant mechanism of MH/PS composites was proposed. It is indicated that MH gradually decomposes and changes into MgO with the rise of thermal treatment temperature and the elongation of thermal treatment time. Under identical conditions, the flame retardancy of t-MH/PS composite decreases noticeably than that of its MH/PS counterpart, but it is still much better than that of pure PS. In addition, the MgO produced by decomposition of MH can promote charring of PS. It is believed that the flame retardant mechanism of MH/PS composites derives from the synergistic effect of the following factors: (1) the cooling effect from endothermal degradation of MH; (2) the gas phase diluting effect of water vapor from degradation of MH; (3) the solid phase obstructing and shielding effect of MgO from degradation of MH; (4) the fire-proof effect from charring of PS induced by MgO.
参考文献
| [1] | Laoutid F, Bonnaud L, Alexandre M, Lopez-Cuesta J M, Dubois P H. New prospects in flame retardant polymer materials: From fundamentals to nanocomposites [ J ]. Materials Science and Engineering Reports, 2009, 63(3) : 100 -125. |
| [2] | Gui H, Zhang X H, Dong W F, et al. Flame retardant synergism of rubber and Mg(OH)z in EVA composites [J]. Polymer, 2007, 48(9): 2537-2541. |
| [3] | Sener A A, Demirhan E. The investigation of using magnesium hydroxide as a flame retardant in the cable insulation materials by cross - linked polyethylene [J ]. Materials and Design, 2008, 29(7)- 1376-1379. |
| [4] | Xu Tao, Huang Xiaoming, Zhao Yongli. Investigation into the properties of asphalt mixtures containing magnesium hydroxide flame retardant [J].Fire Safety Journal, 2011, 46 (6) : 330-334. |
| [5] | Marosfoi B B, Garas S, Bodzay B, et al. Flame retardancy study on magnesium hydroxide associated with clays of different morphology in polypropylene matrix[J].Polymers for Advanced Technologies, 2008, 19(6): 693-700. |
| [6] | Chiu S H, Wang W K. The dynamic flammability and toxicity of magnesium hydroxide filled intumescent fire retardant polypropylene [J].Journal of Applied Polymer Science, 1998, 67(6) : 989-995. |
| [7] | Weil E D, Levchik S, Moy P. Fire and smoke retardants in vinyl chloride polymers- Commercial usage and current developments[J]. Journal of Fire Science, 2006, 24(3): 211-218. |
| [8] | 陈玉坤,徐传辉,贾德民,等.Mg(OH)2阻燃聚合物的研究进展[J].合成树脂及塑料,2007,24(2):64-68. |
| [9] | RothonR N, Hornsby P R. Flame retardant effects of magnesium hydroxide [J]. Polymer Degradation and Stability, 1996, 54(2): 383-385. |
| [10] | Kim S. Flame retardancy and smoke suppression of magnesium hydroxide filled polyethylene[J].Journal of Polymer Science, Part B: Polymer Physics, 2003, 41(9): 936 -944. |
| [11] | Yeh J T, Yang H M, Huang S S. Combustion of polyethylene filled with metallic hydroxides and crosslinkable polyethylene [J]. Polymer Degradation and Stability, 1995, 50(2) :229-234. |
| [12] | Larry K. Magnesium hydroxide: Halogen-free flame retardant and smoke suppressant for polypropylene [J].Plastics Compounding, 1985, 9(4): 40-44. |
| [13] | Hull T R, Witkowski A, Hollingbery L. Fire retardant action of mineral fillers[J].Polymer Degradation and Stability, 2011, 96(8): 1462-1469. |
| [14] | 黄国波,高建荣,贾建洪,等.有机磷氮系一蒙脱土/LDPE纳米复合材料的制备及阻燃性能[J].复合材料学报,2010,27(6):45-52. |
| [15] | Carty P, White S. Char formation in polymer blends [J]. Polymer, 1994, 35(2): 343-347. |
| [16] | Carty P, White S. Iron-chlorine interaction in blends of poly (vinyl chloride) and acrylonitrile-butadiene-styrene containing basic iron( IR )oxide [J]. Polymer, 1995, 36(5): 1109-1111. |
| [17] | Carty P, White S. Flammability of polymer blends [J]. Polymer Degradation and Stability, 1996, 54(2): 379-381. |
| [18] | Carpentier F, Bourbigot S, Bras M, et al. Charring of fire retarded ethylene vinyl acetate copolymer - magnesium hydroxide/zinc borate formulations [J]. Polymer Degradation and Stability, 2000, 69(1): 83-92. |
| [19] | 刘继纯,陈权,井蒙蒙,等.PS/PPO合金的燃烧行为研究[J].塑料科技,2011,39(4):35-39. |
| [20] | 李斌,王建棋.聚合物材料燃烧性和阻燃性的评价--锥形量热仪(Cone)法[J].高分子材料科学与工程,1998,14(5):15-19. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%