利用对-硝基苯基重氮氟硼酸盐和聚酰胺酸进行重氮偶合反应,然后再经过酰亚胺化反应,合成了侧链含偶氮染料发色团的聚酰亚胺非线性光学材料(NLOPI).采用能量为30 keV,剂量为6.0×1016ions/cm2的氮离子对NLOPI进行离子注入改性.通过傅里叶变换红外光谱(FT-IR)、紫外-可见吸收光谱(UV-Vis)、X射线粉末衍射(XRD)、热失重分析(TGA)和扫描电镜(SEM)对离子注入改性NLOPI的微观结构和热稳定性能进行研究.研究表明,离子注入改性后的NLOPI在3426 cm-1和1653 cm-1处出现N-H的振动吸收峰;在400 nm～600 nm的可见光区域的吸收强度减小;离子注入使NLOPI的分子链排列更加规整,取向度明显增加,结晶性能有所改善,但仍是非晶态聚合物;离子注入后NLOPI的起始分解温度为320 ℃,材料的热稳定性能显著增强.
参考文献
| [1] | Churikov VM.;Lin JT.;Wu HH.;Lin JH.;Huang TH.;Hsu CC. .One- and two-photon induced molecular conformation change and reorientation and related third-order nonlinearities in phenylamine azo-dye polymer thin films[J].Optics Communications: A Journal Devoted to the Rapid Publication of Short Contributions in the Field of Optics and Interaction of Light with Matter,2002(4/6):451-460. |
| [2] | Van den Broeck K;Verbiest T;Degryse J et al.[J].Polymer,2001,42(08):3315. |
| [3] | Wasserman B .[J].Physical Review,1986,34(03):1926. |
| [4] | Ratier B;Pelous Y;Froyer G et al.[J].Synthetic Metals,1991,41-43:1483. |
| [5] | Aleshin AN.;Suvorov AV.;Usov IO.;Conklin JA.;Su TM. Kaner RB.;Mironkov NB. .Conductivity and magnetoconductivity of polyaniline films implanted with Ar+ and Ga+ ions near the critical regime of the metal-insulator transition[J].Journal of Physics. Condensed Matter,1998(22):4867-4875. |
| [6] | Rao G R;Wang I L;Lee E H .[J].Journal of Materials Research,1993,8(04):927. |
| [7] | Lee E H;Lewis M B;Blau P J et al.[J].Journal of Materials Research,1991,6(03):610. |
| [8] | 孙建平,吴洪才,李宝铭,应祖金.侧链含偶氮苯发色团的聚酰亚胺薄膜的制备及其三阶非线性光学和光存储性能的研究[J].高等学校化学学报,2004(02):372-375. |
| [9] | 孙建平,吴洪才,李宝铭,应祖金.侧链含偶氮非线性光学活性基团的聚酰亚胺的合成与表征[J].西安交通大学学报,2003(06):646-649. |
| [10] | 吴洪才.离子注入聚丙烯对其结晶及陷阱电荷的影响[J].高分子材料科学与工程,1988(03):35-41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%