<正> 对于 Pr-Fe 二元系,Ray 等早期研究确定有六方晶系 PrFe_7(a=8.582,c=12.461)存在.文献指出:在常压下只存在 Pr_2Fe_7,而在一定压力下还有 PrFe_2.文献表明有Pr_2Fe_(17)和 PrFe_2,分别在1100和670℃由包晶反应生成,共晶反应(80-85at.-%Pr)温度为660℃,但对 PrFe_2的存在尚未肯定,而且未测出液相线.我们的实验,采用纯度99.95%Pr 和99.99%Fe,共配制各重3g的38个合金试样,在氩气保
A recommended phase diagram of the binary Pr-Fe system is presented from X-ray diffraction and μDTA data.In this system,the intermetallic compounds Pr_2Fe_(17) and PrFe_2 exist and decompose at peritectic reaction temperature 1310 and 1100℃ respectively.It undergoes eutectic reaction at 90.0 at.-% Pr at about 610℃,Neither Pr in Fe nor Fe in Pr indicates any detectable solid solubility,