以La2O3和尿素为原料,丙三醇为分散剂,采用均相沉淀方法制备镧盐前驱体,并通过H2S硫化得到γ-La2S3粉体.采用X射线衍射仪和扫描电子显微镜对镧盐前驱体和γ-La2S3粉末的结构和形貌进行表征.结果表明,当加热温度为95℃,尿素和La2O3的物质的量比为15∶1,V(丙三醇)/V(水)=1∶1,反应时间为3h时,可制备出高纯、分散性好、球形γ-La2S3纳米粉体.
参考文献
| [1] | Bor Jou Tsay .A study on infrared transmission of lanthanum sulfide and oxysulfide in the 2.5-14 μm region[J].Materials Letters,1998(3/6):180-183. |
| [2] | 王向阳.8-14μm红外波段的窗口材料[J].人工晶体学报,1995(04):358. |
| [3] | 施剑林;冯涛.无机光学透明材料-透明陶瓷[M].上海:上海科学普及出版社,2008:3-7. |
| [4] | 秦海明,刘宏,桑元华,张晓琳,吕耀辉,王继扬.合成条件对尿素沉淀法制备氧化钇纳米微球的影响[J].人工晶体学报,2011(06):1455-1459. |
| [5] | Jieqiang Wang;Shaohua Zheng;Rong Zeng .Microwave Synthesis of Homogeneous YAG Nanopowder Leading to a Transparent Ceramic[J].Journal of the American Ceramic Society,2009(6):1217-1223. |
| [6] | Kumta P N;Dravid V P;Risbud S H .Structural Characterization of Chemically Synthesized Cubic Lanthanum Sulphide (γ-La2S3)[J].PHILOSOPHICAL MAGAZINE B-PHYSICS OF CONDENSED MATTER STATISTICAL MECHANIC,1993,68(01):67-84. |
| [7] | Li, P.;Jie, W.;Li, H. .Infrared transmission of Na~+-doped γ-La_2S _3 ceramics densified by hot pressing[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2011(9):095402-1-095402-5. |
| [8] | 刘颖,冯金朝.燃烧法制备La_2O_3纳米晶的研究[J].人工晶体学报,2009(06):1489-1492. |
| [9] | 肖劲,万烨,周峰,秦琪,陈燕彬.尿素均匀沉淀法制备超细α-Al2O3粉体[J].中国有色金属学报,2007(05):783-788. |
| [10] | 卢歆 .Yb<'3+>：Y<,2>O<,3>透明陶瓷超细粉体的制备及性能研究[D].长春理工大学,2008. |
| [11] | 卫志贤;刘荣杰;郑岚 等.均匀沉淀法制备纳米氧化物工艺分析[J].西北大学学报(自然科学版),1998,28(05):407-411. |
| [12] | 刘家祥,丁德玲,王震,韩跃新.均匀沉淀法制备纳米氧化锌[J].有色金属,2006(01):49-52. |
| [13] | 金志浩;高积强;乔冠军.工程陶瓷材料[M].西安:西安交通大学出版社,2000 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%