分别采用热压、低电场强度和高电场强度3种工艺烧结制备Bi1.2Sb4.8Te9热电材料,测试、对比分析3组试样的微观结构和热电传输性能。结果表明,采用电场加热方式烧结可有效提高材料的致密度,且在大电场强度工艺下晶粒择优取向。电场可使材料内缺陷减少,载流子浓度下降,同时提高载流子迁移率,使材料综合电性能提高,晶粒择优取向有助于降低材料热导率,这些都有助于热电材料ZT值的提高。
Thermoelectric materials Bi1.2 Sb4.8 Te9 was sintered under three different conditions including no-cur- rent sintering (NCS), low-current density sintering (LCS) and high-current density sintering (HCS). The mi- crostructure and thermoelectric performance of three groups' samples were tested and compared. The results indicated that the applying of electric current in the sintering process can significantly improve the densifieation of samples, and the large electric field can make the grains oriented at the direction of the electric field. The e- lectric field can eliminate crystal defects, and decrease the carrier concentration, and increase the carrier mobili- ty. Thus the power factor was enhanced. The preferred orientation of grains can decrease the thermal conduc- tivity. Therefore, a large electric field and high electric current in the sintering process may be the effective way to obtain thermoelectric materials with high value of the figure of merit ZT.
参考文献
| [1] | Rowe D M.General principles and basic considerations of thermoelectric handbook[M].Boca Raton:crc Press,2005:3. |
| [2] | Zheng Youjin;Ma Hong'an;Jia Xiaopeng .Study on high pressure and heat-treatment of β-FeSi2 synthesized[J].Journal of Functional Materials,2011,42:964-969. |
| [3] | Meng Qingsen;Fan Wenhao;Chen Ruixue et al.Ther- moelectric properties of nanostructured FeSiz prepared by field-activated and pressure-assisted reactive sintering[J].Journal of Alloys and Compounds,2010,492:303-306. |
| [4] | Jiang Hongyi .Study on the solid-state reaction synthesis,preparation and thermoelectric properties of Mg-Si based compounds[D].Wuhan:Wuhan University of Technolo- gy,2003. |
| [5] | 张庆云,路清梅,张久兴,张艳峰.放电等离子烧结工艺对Ca3Co4O9陶瓷织构及电性能的影响[J].稀有金属材料与工程,2007(z3):413-416. |
| [6] | Chien-Neng Liao;Li-Chieh Wu;Jinn-Shing Lee .Thermoelectric properties of Bi-Sb-Te materials prepared by electric current stressing[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2010(1/2):468-471. |
| [7] | Plechfi6ek T;Navraitil J;Horak J et al.Point and struc- tural defects in Bi2Pb,Te.3single crystals[J].Solid State Ionics,2007,177:3513-3519. |
| [8] | Hamachiyo T;Ashida M;Hasezaki K .Thermal conduc- tivity of Bi0.sSbl.sTe3 affected by grain size and pores[J].Journal of Electronic Materials,2009,38:1048-1051. |
| [9] | Zhang Qian .Alloying and compositing of Mg2(Si,Sn)based thermoelectric materials[D].杭州:浙江大学,2008. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%