为了测试混合吸附剂基质材料石墨的传热传质特性,设计了吸附剂渗透率与导热系数测试装置,首先用平板热源法测试了散装石墨在不同膨胀温度及不同膨胀时间下的导热系数,优选出了石墨的最佳膨胀工艺,然后采用最佳膨胀工艺下的石墨进行固化,以氮气作为气源对固化石墨进行了渗透率研究,以稳态热源加热法对固化石墨进行导热系数测试,结果表明,当固化密度从100～500 kg/m~3变化时,渗透率介于10~（-15）～10~（-12）之间变化,导热系数则介于1.7～3.2W/（m·K）之间变化。
Adsorbent permeability and thermal conductivity test units were designed to study the heat and mass transfer performances of the host material,i.e.expanded graphite,of compound adsorbent.Firstly the plate heat source method was used to test the thermal conductivities of granular expanded graphite at different expanded temperatures and different values of expansion time,and then the optimal expansion process is selected.Secondly the optimal expansion process is adopted for compacting processes of expanded graphite.After that the permeabilities were tested with nitrogen as the gas source,and the heat conductivities were studied with steady-state heat source heating method. The results show that when the curing density changed from 100 kg/m~3 to 500 kg/m~3,the permeability varied between 10~（-15）～10~（-12）,the thermal conductivity ranged from 1.7 W/（m·K） to 3.2 W/（m·K）.
参考文献
| [1] | Mills A;Farid M;Selman JR;Al-Hallaj S .Thermal conductivity enhancement of phase change materials using a graphite matrix[J].Applied thermal engineering: Design, processes, equipment, economics,2006(14/15):1652-1661. |
| [2] | Ahmet Sari;Ali Karaipekli .Thermal conductivity and latent heat thermal energy storage characteristics of paraffin/expanded graphite composite as phase change material[J].Applied thermal engineering: Design, processes, equipment, economics,2007(8-9):1271-1277. |
| [3] | S. Mauran;H. Lahmidi;V. Goetz .Solar heating and cooling by a thermochemical process. First experiments of a prototype storing 60 kW h by a solid/gas reaction[J].Solar Energy,2008(7):623-636. |
| [4] | Lu HB.;Spinner B.;Mazet N. .MODELLING OF GAS-SOLID REACTION - COUPLING OF HEAT AND MASS TRANSFER WITH CHEMICAL REACTION[J].Chemical Engineering Science,1996(15):3829-3845. |
| [5] | X.Py;E.Daguerre;D.Menard .Composites of expanded natural graphite and in situ prepared activated carbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(8):1255-1265. |
| [6] | Hans-Peter Klein;Manfred Groll .Heat transfer characteristics of expanded graphite matrices in metal hydride beds[J].International journal of hydrogen energy,2004(14):1503-1511. |
| [7] | 李廷贤,王如竹,陈恒,王丽伟,吴静怡.采用固化复合吸附剂的热化学吸附式低温冷冻系统的性能[J].化工学报,2008(z2):192-198. |
| [8] | R.G. Oliveira;R.Z. Wang .A consolidated calcium chloride-expanded graphite compound for use in sorption refrigeration systems[J].Carbon: An International Journal Sponsored by the American Carbon Society,2007(2):390-396. |
| [9] | L. W. Wang;R. Z. Wang;J. Y. Wu;K. Wang .Compound adsorbent for adsorption ice maker on fishing boats[J].International Journal of Refrigeration,2004(4):401-408. |
| [10] | Jong Hun Han;Kun-Hong Lee .Gas permeability of expanded graphite-metallic salt composite[J].Applied thermal engineering: Design, processes, equipment, economics,2001(4):453-463. |
| [11] | S.Biloe;S.Mauran .Gas flow through highly porous graphite matrices[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(3):525-537. |
| [12] | 王凯,吴静怡,王如竹.氯化钙/膨胀石墨混合吸附剂导热性能测试[J].上海交通大学学报,2008(01):106-109. |
| [13] | Z. Tamainot-Telto;R. E. Critoph .Monolithic carbon for sorption refrigeration and heat pump applications[J].Applied thermal engineering: Design, processes, equipment, economics,2001(1):37-52. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%