采用3.4-聚乙烯二氧噻吩(PEDT)溶胶作为导电材料,利用溶胶-凝胶法制备了SiO2-PEDT复合抗静电薄膜.利用平氏粘度计研究了正硅酸乙酯水解与缩聚反应时水的加入量R对复合溶胶性质的影响;用光学显微镜观察薄膜表面结构;利用表面电阻仪研究薄膜的导电性能;用分光光度计考察薄膜的光学性能.研究表明,随水的加入量R的增大,溶胶粘度先增大后减小,在R=4时达到最大值;复合溶胶的胶凝时间缩短;膜层中的粒子增大,变密集,涂层质量降低;膜层的表面电阻逐渐增大.透过率随R增加先降低后升高,在R=4时出现最低值.
参考文献
| [1] | 蒋洋;肖光华;梁开明 .Preparation of Sol-Gel Thin Films on Glass Surface[J].材料导报,1999,13(04):28-31. |
| [2] | 孙继红,范文浩,吴东,孙予罕.溶胶-凝胶（Sol-gel）化学及其应用[J].材料导报,2000(04):25-29. |
| [3] | 杨辉;丁子上;江仲华 .Sol-Gel Kinetic Research of Si(OEt)4[J].硅酸盐学报,1989,17(03):204-209. |
| [4] | Duran A;Serna C;Fornes V et al.Structure Evolution of Sol-Gel System through Viscosity Measurement[J].Journal of Non-Crystalline Solids,1988,106:242-246. |
| [5] | Boonstra A H;Bernards T N M .The Dependence of the Gelation Time on the Hydrolysis Time in a Two-Step SiO2 Sol-Gel Process[J].Journal of Non-Crystalline Solids,1988,105:207-213. |
| [6] | 周耀;张华民;赵修仁 .Investigation of Silica Membrane Prepared by Sol-Gel Process[J].硅酸盐学报,1995,23(01):73-78. |
| [7] | 杨辉;丁子上;江仲华 .The Polycondensation Process for Si(OEt)4Hydrolyzed Products[J].特种玻璃,1990,7(03):22-28. |
| [8] | 葛蔓珍;杨辉;江仲华 .[J].硅酸盐通报,1993,5:32-37. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%