针对目前各种碳化深度测量方法的弊端,结合所发明的检测装置,形成了一套新型抗碳化性能测试方法一碳酸盐含量法.试验结果表明,这是一种更加精确的碳化测试方法,不仅能划分完全碳化区和碳化进行区,还不会因受到其它水泥石中性化因素的干扰而影响测量结果.基于试验结果,对比酚酞喷涂法,说明该方法更具有优势,不但原理简单,而且可以测得试件碳化部分全部的碳化产物含量.
参考文献
| [1] | Qian Jueshi.Materials Science[M].武汉:武汉大学出版社,2007 |
| [2] | Zhuang Yinghao .[J].China Concerete and Cement Products,1987,2:21-22. |
| [3] | Daniel Constantiner.Factors Affecting Concrete Pore Solution (A) Alkali fixation induced by drying and carbonation and (B) Alkali released from feldspars[M].Purdue university,2003:29-40. |
| [4] | Zhang Yu.Introduction to the Durability of Concrete Structures[M].上海:上海科学技术出版社,2003:50-60. |
| [5] | Lin Wei;Lu Xinying .[J].China Concerete and Cement Products,2002,3:10-12. |
| [6] | Yingyu L;Guidong W.The Mechanism of Carbomation of Mortar and the Dependence of Carbonation on Pore Structure[A].Atlanta,1987:1915-1943. |
| [7] | Houst Y F;Wittmann F H .[J].Cement and Concrete Research,1994,24:1165-1176. |
| [8] | 饱和盐溶液标准相对湿度值[M].全国物理化学计量技术委员会,2000 |
| [9] | 杨南如;岳文海.无机非金属材料图谱手册[M].武汉:武汉工业大学出版社,2000:1-100,201-250. |
| [10] | 万朝均;张廷雷;陈璐圆 等.水泥基材料抗碳化性能的测试装置及方法[P].中国专利:200910191152.3,2009-10-19. |
| [11] | 金伟良.混凝土结构耐久性[M].北京:科学出版社,2002:16-46. |
| [12] | 陆平.水泥材料科学导论[M].上海:同济大学出版社,1989:164-213. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%