采用单向硼/环氧复合材料补片真空袋压工艺单面修复含中心裂纹不同厚度铝合金板,测试了修复试件的疲劳性能,从疲劳寿命、疲劳裂纹扩展速率和裂纹扩展纹线考察不同厚度铝合金板修复后疲劳性能的差异.结果表明:硼/环氧补片胶接修复后,铝合金板的疲劳寿命大幅度提高,且疲劳寿命提高幅度随铝合金板厚度增大而降低.厚度为1.76 mm、5.20 mm和10.20 mm 3种铝合金板修复试件的疲劳寿命分别是未修复试件的22.30倍、12.84倍和8.40倍.厚度为1.76 mm铝合金板修复试件在铝合金板完全断裂后还能继续承担疲劳载荷,而厚度为5.20 mm和10.20 mm 2种铝合金板修复试件在铝合金板断裂后完全破坏.裂纹扩展速率和归一化裂纹长度差均随铝合金板厚度增大而增大.
参考文献
| [1] | Baker A A.Repair of cracked or defective metallic aircraftcomponents with advanced fibre composites[J].Composite Structure,1984,2:153-234. |
| [2] | Erdogan F,Arin K A.Sandwich plate with a part-through and a debonding crack[J].Engineering Fracture Mechanics,1972(2):449-458. |
| [3] | Sabelkin V,Mall S,Avran J B.Fatigue crack growth analysis of stiffened cracked panel repaired with bonded composite patch[J].Engineering Fracture Mechanics,2006(11):1553-1567. |
| [4] | Schubbe J J.Thickness effects on a cracked aluminum plate with composite patch repair[D].Ohio,USA:Air Force Institute of Technology of Wright-Patterson AFB,1997. |
| [5] | Labor J G,Ratwani M M.Development of bonded composite patch repairs for cracked metal structures final report,NADC-79066-60[R].Warminster.United States NavyNaval Air Development Center,PA 18974,1980. |
| [6] | Okafor A C,Singh N,Enemuoh U E,et al.Design,analysis and performance of adhesively bonded composite patch repair of cracked aluminum aircraft panels[J].Composite Structures,2005,71:258-270. |
| [7] | Hosseini-Toudeshky H.Effects of composite patches on fatigue crack propagation of single-side repaired aluminum panels[J].Composite Structures,2006,76:243-251. |
| [8] | Hosseini-Toudeshky H,Bakhshandeh S,Mohammadi B,et al.Experimental investigations on fatigue crack growth of repaired thick aluminium panels in mixed-mode conditions[J].Composite Structures,2006,75:437-443. |
| [9] | Tai G C,Shen S B.Fatigue analysis of cracked thick aluminum plate bonded with composite patches[J].Composite Structures,2004,64:79-90. |
| [10] | 蔡洪能,陆玉姣,王雅生,等.FRP补强疲劳损伤钢结构裂纹扩展研究[J].材料工程,2006(增刊),378-381.Cai Hongneng,Lu Yujiao,Wang Yasheng,et al.Fatigue damaged crack growth of steel structure strengthened with FRP patches[J].Material Engineering,2006(Suppl):378-381. |
| [11] | 杨孚标,肖加余,江大志,等.炭纤维/环氧复合材料单面修补中心裂纹铝合金板的静态和疲劳特性[J].复合材料学报,2007,24(3):1-6.Yang Fubiao,Xiao Jiayu,Jiang Dazhi,et al.Static characteristics and fatigue behavior of the center-cracked aluminum plates one-sidedly bonded with composite patches[J].Acta Materiae Compositae Sinica,2007,24(3):1-6. |
| [12] | Pairs P C,Gomez M P,Anderson W P.A rational analytic theory of fatigue[J].The Trend of Engineering,1961,13:9-14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%