在硅铝复合电解液中,采用不同的电参数在AZ91D镁合金表面制备微弧氧化膜。利用扫描电镜（SEM）观察了膜层表面微观形貌;通过膜层测厚仪测量了氧化膜的厚度。结果表明,随着电流密度、占空比或者氧化时间的增大,膜层的不均匀程度都逐渐增大,表面放电孔洞尺寸变大,数量减少;电流密度大于10A/dm2或氧化时间超过15min时,微弧氧化过程会出现熄弧阶段;膜层厚度随着电流密度的增加而呈现近似线性增加后趋于稳定的变化趋势;而随着占空比或者氧化时间的延长,膜层厚度则逐渐增大。
Ceramic coatings on AZ91D magnesium alloy were prepared by microarc oxidation with different electrical parameters in a silicate-aluminate dual electrolyte solution.Surface morphology and film thickness of the coating were characterized by scanning electron microscopy（SEM） and layer thickness meter.The results showed that the non-uniformity of the coating increased gradually with increasing the current density,duty cycle and oxidation time.The diameter of the discharge aperture increased but the number of discharge apertures decreased with increasing the current density,duty cycle and oxidation time.Extinguish arc stage appeared during the process of micro-arc oxidation when the current density was more than 10 A/dm2 or the oxidation time was more than 15 minutes.With the increase of current density,the thickness of the coating increased linearly first and then kept in a constant.Similarly,the thickness of the coating increased gradually with the increase of the duty cycle and oxidation time.
参考文献
| [1] | 李海燕,张世珍,孙春龙.镁合金的腐蚀与表面处理进展[C].2009’水环境腐蚀与防护学术研讨会论文集,2009:16-21. |
| [2] | J.E. Gray;B. Luan .Protective coatings on magnesium and its alloys-a critical review[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):88-113. |
| [3] | 张玉海.镁合金表面处理技术的研究进展[J].材料保护,2008(03):55-57. |
| [4] | 王莹,张津,麻彦龙,吴超云.镁合金表面处理新进展[J].表面技术,2006(06):61-64. |
| [5] | Comparison of electrochemical corrosion behaviour of MgO and ZrO_2 coatings on AM50 magnesium alloy formed by plasma electrolytic oxidation[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(10):2483. |
| [6] | P. Bala Srinivasan;C. Blawert;W. Dietzel .Dry sliding wear behaviour of plasma electrolytic oxidation coated AZ91 cast magnesium alloy[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2009(11/12):1241-1247. |
| [7] | Tang, Y.;Zhao, X.;Jiang, K.;Chen, J.;Zuo, Y. .The influences of duty cycle on the bonding strength of AZ31B magnesium alloy by microarc oxidation treatment[J].Surface & Coatings Technology,2010(6):1789-1792. |
| [8] | Gnedenkov, SV;Khrisanfova, OA;Zavidnaya, AG;Sinebryukhov, SL;Egorkin, VS;Nistratova, MV;Yerokhin, A;Matthews, A .PEO coatings obtained on an Mg-Mn type alloy under unipolar and bipolar modes in silicate-containing electrolytes[J].Surface & Coatings Technology,2010(14):2316-2322. |
| [9] | 樊向,姚晓菊.电流密度对微弧氧化热损耗和膜层致密性的影响[J].腐蚀与防护,2011(03):197-199. |
| [10] | 郭洪飞,安茂忠,徐莘,霍慧彬.电流密度对镁合金微弧氧化过程及氧化陶瓷膜性能的影响[J].稀有金属材料与工程,2005(10):1554-1557. |
| [11] | 陈显明,罗承萍,刘江文,李文芳.镁合金微弧氧化膜层形成过程探讨[J].中国表面工程,2006(05):14-18,21. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%