在室温对完全时效7003铝合金进行4道次ECAP (Bc)挤压,成功获得大约200 nm至几百纳米的超细晶粒.借助透射电镜(TEM)观察ECAP变形过程中的微观组织特征,如位错缠绕区(DTZ)、位错胞结构、孤立位错胞(IDC)、稠密位错墙(DDW)、胞块(CB)、显微带(MB)和S带等.7003铝合金在变形过程中的细化机制主要是位错分割机制.
参考文献
| [1] | 赵西成,王幸运,杨西荣,王成,刘晓燕.120°模具室温8道次ECAP变形TA1纯钛的组织与性能[J].稀有金属材料与工程,2011(01):28-31. |
| [2] | Ruslan Z. Valiev;Terence G. Langdon .Principles of equal-channel angular pressing as a processing tool for grain refinement[J].Progress in materials science,2006(7):881-981. |
| [3] | Cardoso, K.R.;Travessa, D.N.;Botta, W.J.;Jorge, A.M. .High Strength AA7050 Al alloy processed by ECAP: Microstructure and mechanical properties[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(18):5804-5811. |
| [4] | 陈克华;梁伟;王顺旗 et al.[J].稀有金属材料与工程,2011,39(02):352. |
| [5] | Sha Gang;Yao Lan;Liao Xiaozhou et al.[J].Ultramicroscopy,2011,111(06):500. |
| [6] | Shehreen S Dheda;Farghalli A Mohamed .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2011,528(28):8179. |
| [7] | 毕见强,孙康宁,刘睿,范润华,王素梅.等径角挤压2A12铝合金超细晶组织结构研究[J].特种铸造及有色合金,2006(01):1-4. |
| [8] | Huang J Y;Zhu Y T;Jiang H et al.[J].Acta Materialia,2001,49(09):1497. |
| [9] | 余永宁.金属学原理[M].北京:冶金工业出版社,2007:408. |
| [10] | 周玉;武高辉.材料分析测试技术-材料X射线衍射与电子显微分析[M].哈尔滨:哈尔滨工业大学出版社,2007:197. |
| [11] | 杨刚;张凌义;王立明 .[J].特钢技术,2008,55(02):1. |
| [12] | Segal VM .Equal channel angular extrusion: from macromechanical to structure formation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):322-333. |
| [13] | Estrin Y;Tóth L S;Molinari A et al.[J].Acta Materialia,1998,46(15):5509. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%