Cr2O3薄膜具有保护性,采用电沉积-热解法制备还未见报道.采用电沉积-热解法在304不锈钢表面制备Cr2O3薄膜,并将其于900℃高温氧化100 h,研究了电沉积溶液[Cr(NO3)3酒精]浓度、沉积电压对Cr2O3薄膜抗高温氧化性能的影响,分析高温氧化样的组织结构.结果表明:电沉积-热解法制备的Cr2O3薄膜显著提高了304不锈钢的抗高温氧化性能;沉积电压为25 V,电沉积溶液浓度为0.10 mol/L条件下制备的Cr2O3薄膜抗高温氧化性能最佳.
参考文献
| [1] | Jing Ma;Yedong He;Wei Gao;Jun Wang;Baode Sun .The effect of micro-crystallizing on the oxidation resistance of Cu–Cr alloy in air[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):311-317. |
| [2] | Ma J;He Y D;Sun B D et al.The oxidation of micro-crystalline Co-Cr alloys under balanced oxygen pressure of Co2O3/Co powders[J].Journal of Materials Processing Technology,2008,202:457-463. |
| [3] | 马静,郭俐聪,张彦超,何业东.喷丸处理对1Cr13钢选择氧化的作用[J].河北科技大学学报,2007(03):226-229. |
| [4] | 马静,何业东,胡建文,田建辉.退火处理对喷丸处理1Cr18Ni9Ti合金选择氧化的影响[J].材料热处理学报,2004(03):46-49. |
| [5] | Jing Ma;Yedong He;Deren Wang .The effects of pre-oxidation and thin Y_2O_3 coating on the selective oxidation of Cr18-Ni9-Ti steel[J].Materials Letters,2004(5):807-812. |
| [6] | Ma J;He Y D;Wang D R et al.Effects of Pre-Oxidation on Selective Oxidation Behavior of Fe-25Cr-7Ni-N Alloy[J].High Temperature Materials and Processes,2004,23(1):7-12. |
| [7] | Ma J;He Y D;Wang J et al.High temperature corrosion behavior of microcrystalline aluminide coating on Q235 steel[J].Corrosion Engineering,Science and Technology,2009,44(2):157-160. |
| [8] | 秦磊,彭徽,郭洪波,宫声凯,徐惠彬.DZ125合金再涂覆CoCrAlY涂层界面互扩散行为研究[J].金属学报,2013(02):229-235. |
| [9] | 马静,何业东,王俊,孙宝德.Y2O3薄膜处理对3Cr25Ni7N合金的抗高温氧化性能的影响[J].中国稀土学报,2007(06):765-768. |
| [10] | 马静,何业东,王俊,孙宝德.1Cr13合金沉积Y2O3薄膜后的高温氧化行为[J].材料保护,2008(07):21-22,44. |
| [11] | 马静,陈维视,何业东.电沉积-热解法制备Ce2O3薄膜的抗氧化性能研究[J].河北科技大学学报,2006(03):224-226,229. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%