化学镀法制备Ni包覆ZrO2微粉，用分光光度法测定了镀液中的镍含量与时间的关系．得出NaF、表面活性剂对镀覆反应的影响，计算了镀覆反应的表现活化能．结果表明，镀覆后颗粒均由Ni和ZrO2两种成份复合而成，达到了均匀分散金属相和陶瓷相的目的；NaF和表面活性剂均能降低反应的表观活化能．
In the process of electroless plating used to Ni coated ZrO2 ultrafine powders, the relationship between Ni2+ concentration in solution
and time at different temperatures was determined. The effect of Ni2+ concentration, NaF and surfactants on the speed of Ni deposit was obtained.
Apparent activity energy was concluded. The goal that even mixing Ni with ZrO2 was attained. Experimental results show that
Ni is coated on ZrO2 powder surface and the speed of Ni deposit can be raised and apparent activity energy can be dropped by NaF and surfactants.
参考文献
| [1] | 黄培云主编. 粉末冶金原理. 北京：冶金工业出版社， 1982. 8--80 2 余家国，袁国章，朱颉安. 武汉工业大学学报，1991， 13 (1): 44--51 3 王耀宏. 材料保护，1995， 28 (1): 34--35 4 梁焕珍，孙京成，黄建忠等. 化工冶金，1984， 5 (3): ?8--23 5 熊晓东，田彦文，翟秀静等. 中国有色金属学报，1996， 6 (4): 39--42 6 Levy R A. Electrochemical Technology, 1963, 1 (1-2): 38--42 7 邵忠财，翟玉春，田彦文. 材料保护，1998， 31 (2): 19--20 8 邵忠财，田彦文，翟玉春. 东北大学学报，1998， 19 (S1): 304--306 9 翟金坤，黄子勋. 化学镀镍. 北京：北京航空学院出版社，1987. 1--20 10 黄安，高军. 电镀与环保，1996，1 6 (3): 6--8 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%