Austempered ductile iron (ADI) has several advantages of replacing cast steel and forged steel in many engineering fields. A new Mn-Cu alloyed ADI with excellent mechanical properties has been developed in order to cut the cost and enlarge the application of ADI. The helical bevel gears were made of the new-developed Mn-Cu alloyed ADI. The microstructure and mechanical properties of the standard sample were investigated by optical microscope (OM), scanning electron microscope (SEM) and performance measurement. The results showed that after a series of treatments, the mechanical properties (Rm 10074 to 1200 MPa, A 52% to 88%, HRC 32 to HRC 35, αK 70 to 120 J/cm2) of the Mn-Cu alloyed ADI standard sample could reach European standard EN1564-97/ EN-CJS-1000-5. The surface hardness after helical bevel gears meshing was significantly increased due to the formation of martensite. The bench test and traffic running testing results suggested that the new Mn-Cu alloyed ADI with ultimate life and median life respectively exceeding 30×104 and 50×104 times could replace 20CrMnTi forged steel for manufacturing the EQ140 helical bevel gears.
参考文献
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%