目的在1.2344钢表面获得一层硬度较高的强化层。方法利用强流脉冲电子束技术，在相同的加速电压下，采用不同的脉冲次数对1.2344钢表面进行改性处理，研究处理前后样品的表层显微组织和性能变化规律。结果经强流脉冲电子束处理后，试样表面形成了形状各异、大小不一、分布不均的熔坑，并且随着脉冲次数的增加，熔坑数量逐渐减少，熔坑的直径变大。当脉冲次数大于50次时，试样表面出现奥氏体相，表面显微硬度提高了14.5%。结论强流脉冲电子束处理可使试样表层的晶粒变小，晶粒细化和表面宏观残余应力的共同作用促使试样显微硬度增加。
ABSTRACT:Objective To obtain a strengthened layer with high hardness on the surface of 1. 2344 steel. Methods 1. 2344 steel was irradiated with uniform accelerating voltage and different pulses using high-current pulsed eletron beam. The variation rules of surface microstructure and performance of the sample before and after modification were studied. Results It turned out that the sur-face of the samples formed some crater-like defects which had different shapes, sizes and nonuniform distruction after irradiation by HCPEB. The number of crater-like defects was decreased and the diameter was increased with the increasing irradiating pulse. Austenite appeared on the surface of the irradiated samples, and the surface microhardness was increased by nearly 14. 5% when the pulse frequency exceeded 50. Conclusion After processing with high-current pulsed electron beam, the size of the grain was re-duced in the surface layer of the sample. The microhardness of the specimen was increased due to the grain refinement and the gen-eration of macroscopic residual stress.
参考文献
| [1] | 周永权,赵洋,王璞.表面强化技术的研究及其应用[J].机械管理开发,2010(05):104-105. |
| [2] | 樊东黎.中国热处理的过去、现状和未来[J].热处理,2004(03):1-11. |
| [3] | 李茂山,赵宝荣,吴光英,张克俭.我国热处理的现状及发展方向[J].兵器材料科学与工程,1999(02):48-55. |
| [4] | 郝胜智,吴平生,张向东,邹建新,秦颖,董闯.强流脉冲电子束表面处理[J].金属热处理,2008(01):77-81. |
| [5] | 李刚,况军,相珺,邱星武,邱玲.AZ31镁合金强流脉冲电子束表面改性研究[J].材料保护,2009(02):49-51. |
| [6] | D. I. Proskurovsky;V. P. Rotshtein;G. E. Ozur;A. B. Markov;D. S. Nazarov;V. A. Shulov;Yu. F. Ivanov .Pulsed electron-beam technology for surface modification of metallic materials[J].Journal of Vacuum Science & Technology, A. Vacuum, Surfaces, and Films,1998(4):2480-2488. |
| [7] | Stippich F.;Wolf GK.;Berg G.;Friedrich C.;Vera E. .Enhanced corrosion protection of magnesium oxide coatings on magnesium deposited by ion beam-assisted evaporation[J].Surface & Coatings Technology,1998(0):29-35. |
| [8] | D. I. Proskurovsky;V. P. Rotshtein;G. E. Ozur;Yu. F. Ivanov;A. B. Markov .Physical foundations for surface treatment of materials with low energy, high current electron beams[J].Surface & Coatings Technology,2000(1/3):49-56. |
| [9] | 赵铁钧,田小梅,高波,涂赣峰.电子束表面处理的研究进展[J].材料导报,2009(05):89-91. |
| [10] | Ozur GE.;Proskurovsky DI.;Rotshtein VP.;Markov AB. .Production and application of low-energy, high-current electron beams[J].Laser and Particle Beams,2003(2):157-174. |
| [11] | 陈元芳,胡建军,许洪斌,鲜杨,金铁玉.强流脉冲电子束处理下40Cr的摩擦磨损性能研究[J].材料导报,2009(24):60-62. |
| [12] | 关庆丰,安春香,秦颖,邹建新,郝胜志,张庆瑜,董闯,邹广田.强流脉冲电子束应力诱发的微观结构[J].物理学报,2005(08):3927-3934. |
| [13] | Shulov VA.;Remnev GE.;Pellerin F.;Monge-Cadet P.;Nochovnaya NA. .High-power ion beam treatment application for properties modification of refractory alloys[J].Surface & Coatings Technology,1998(1/2):74-81. |
| [14] | 梅显秀,马腾才,王秀敏,徐卫平,宋美丽.强流脉冲离子束辐照W6Mo5Cr4V2高速钢表面改性研究[J].金属学报,2003(09):926-931. |
| [15] | 李生志,李玉海,许婷婷.高速钢M2强流脉冲电子束表面改性研究[J].表面技术,2009(06):24-26,59. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%