研究了一种金属表面硅烷化处理液制备工艺,并对该处理液以及经过处理后钢表面薄膜进行了分析和评价.结果表明:此工艺所得硅烷处理液的性能优良,能够在长时间内具有较好的稳定性及防腐效果.这一结果对开展金属表面硅烷化处理以及相应处理液研究均具有参考价值.
参考文献
| [1] | Liu L,Hu J M,Zhang J Q,et al.Improving the formation and protective properties of silane films by the combined use of electrodeposition and nanoparticles incorporation[J].Electrochim.Acta,2006,52(2):53 |
| [2] | Pan G R,Dale W S.Morphology and water-barrier properties of silane films on aluminum and silicon[J].Thin Solid Films,2006,503(1/2):259 |
| [3] | Bexell U,Mikael G T.A corrosion study of hot-dip galvanized steel sheet pre-treated with gamma-mereaptopropyltrimethoxysilane[J].Surf.Coat.Technol.,2007,201(8):4734 |
| [4] | Graeve I D,Vereecken J,Franquet A,et al.Silane coating of metal substrates:Complementary use of electrochemical,optical and thermal analysis for the evaluation of film properties[J].Prog.Org.Coat.,2007,59(3):224 |
| [5] | 王锡春.硅烷在涂装前处理工艺中的神奇应用[J].上海涂料,2010,48(3):24 |
| [6] | 刘倞,胡吉明,张鉴清等.金属表面硅烷化防护处理及其研究现状[J].中国腐蚀与防护学报,2006,26(1):59 |
| [7] | 陈远.SiO2基有机-无机复合耐腐蚀薄膜的制备与性能研究[D].杭州:浙江大学,2010 |
| [8] | 丁新更,陈远,吴春春等.KH570改性SiO2复合耐腐蚀涂层结构及性能[J].材料工程,2010,(12):72 |
| [9] | 赵磊,鲁文杰.可UV固化的稳定硅溶胶的制备及其应用[J].涂料工业,2012,42(4):56 |
| [10] | 周文娟,许立坤,王佳.缓蚀剂对硅烷锌铝涂层性能的影响[J].腐蚀科学与防护技术,2008,20(4):292 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%