研究薃Z80镁合金经300℃等通道挤压(ECAP)后的组织、织构与力学性能的演变规律以及第二相析出行为的影响.结果表明:ECAP显著促进了粒状连续析出,可有效节省后续热处理时间.A路径多道次挤压最终获得基面织构;Bc路径挤压后形成基面近似平行于剪切面的织构;第二相析出对ECAP织构特征的形成没有显著影响.用该工艺可获得较高的延伸率(13%-19%),但是抗拉强度过低(<300 MPa),综合机械性能不理想.可通过抑制挤压前的未溶粗大粒子的析出、减少挤压遭次和降低挤压温度等措施优化AZ80的析出控制.
AZ80 magnesium alloy was subjected to ECAP (equal channel angular extrusion) processing at 300 ℃. The evolution of microstructure, texture and mechanical properties influenced by the precipitation was investigated. The results show that ECAP processing significantly favored granular-like Mg_(17)Al_(12) continuous precipitation in accompany with reducing time effectively during subsequent aging treatment; basal texture can be obtained via route A after ECAP with multi passes, whereas typical shear texture with most basal planes parallel to the shear plane of mode in route Bc; however the precipitation has not remarkable effect on the texture development during ECAP. A relative low ultimate tensile strength of 300 Mpa and an improved elongation of 19% were obtained in the processed samples due to strong texture and coarse precipitates. Further optimization should be made by means of impeding the precipitation of the coarse particles before ECAP and decreasing the number of pass and pressing temperature.
参考文献
| [1] | S.R.Agnew,J.A.Horbon,T.M.Lillo,D.W.Brown,Enhanced ductility in strongly texture magnesium produced by equal channel angular processing,Scripta Materialia,50(3),377(2004) |
| [2] | B.Chen,D.L.Lin,L.Jin,X.Q.Zeng,C.Lu,Equal-channel angular pressing of magnesium alloy AZ91 and its effect onmicrostructure and mechanical properties,Material Science and Engineering,A483-484,113(2008) |
| [3] | M.Eddahbi,J.A.del Valle,M.T.Pdres-Prado,O.A.Ruano,Comparison of the microstructure and thermal stabilityof an AZ31 alloy processed by ECAP and large strainhot rolling,Material Science and Engineering,A410-411,308(2005) |
| [4] | M.Janecek,M.Popov,M.G.Krieger,R.J.Hellming,Y.Estrin,Mechanical properties and microstructure ofa Mg alloy AZ31 prepared by equal-channel angular pressing,Material Science and Engineering,A462,116(2007) |
| [5] | T.Mukal,M.Yamanoi,H.Watanabe,K.Higashi,Ductility enhancement in AZ31 magnesium alloy by controlling its grain structure,Scripta Materialia,45(1),89(2001) |
| [6] | A.Yamashita,Z.Horita,T.G.Langdon,Improving the mechanical properties of magnesium and a magnesium alloy through severe plastic deformation,Material Science and Engineering,A300,142(2001) |
| [7] | W.J.Kim,C.W.An,Y.S.Kim,S.I.Hong,Mechanical properties and microstructures of an AZ61 Mg Alloy produced by equal channel angular pressing,Scripta Materialia,47(1),39(2002) |
| [8] | LU Linlin,YANG Ping,WANG Faqi,ZHONG Weizhen,Effects of thermomechanical treatments on microstructure and mechanical properties of AZ80 magnesium alloy,The Chinese Journal of Nonferrous Metals,16(6),1034(2006)(路林林,杨平,王发奇,钟伟珍,形变热处理对AZ80镁合金组织及性能的影响,中国有色金属学报,16(6),1034(2006)) |
| [9] | Q.G.Xie,P.Yang,F.E.Cui,Influence of deformation on precipitation and recrystallization in an AZ80 magnesium alloy,Materials Science Forum,546-549,293(2007) |
| [10] | D.Duly,M.Audier,Y.Brechet,On the influence of plastic deformation on discontinuous precipitation in Mg-Al,Scripta Metallurgica et Materialia,29(12),1593(1993) |
| [11] | S.Suwas,G.Gottstein,R.Kumar,Evolution of crystal lographic texture during equal channel angular extrution(ECAE) and its effects on secondary processing of magnesium,Material Science and Engineering,A471,1(2007) |
| [12] | S.Suwas,L.S.T6th,J.J.Fundenberger,A.Eberhardt,Texture evolution in commercially pure Al during equal channel angular extrusion (ECAE) as a function of processing routes,Solid State Phenomena,105,357(2005) |
| [13] | S.Suwas,L.S.Tóth,J.J.Fundenberger,A.Eberhardt,W.Skrotzki,Evolution of crystallographic texture during equal channel angular extrusion of silver,Scripta Materialia,49(12),1203(2003) |
| [14] | CHENG Yongqi,CHEN Zhenhua,Deformation law of equal channel angular rolling for AZ31 magnesium alloy sheets,Journal of Plasticity Engineering,14(4),127(2007)(程永奇,陈振华,AZ31镁合金板材等径角轧制变形规律研究,塑性工程学报,14(4),127(2007)) |
| [15] | Y.Yoshida,L.Cisar,S.Kamado,J.I.Koike,Y.Kojima,Texture development of AZ31 magnesium alloy during ECAE processing,Materials Science Forum,491-422,533(2003) |
| [16] | S.R.Agnew,P.Mehrotra,T.M.Lillo,G.M.Stoica,P.K.Liaw,Crystallographic texture evolution of three wrought magnesium alloys during equal channel angular extrusion,Material Science and Engineering,A408,72(20O5) |
| [17] | M.A.Michael,B.Hugh,ASM Speciality Handbook-Magnesium and Magnesium Alloys (Ohio,ASM International,1999) p.22 |
| [18] | Y.B.Li,Y.B.Chen,H.Cui,B.Q.Xiong,J.S.Zhang,Microstructure and mechanical properties of spray-formed AZ91 magnesium alloy,Materials Characterization,60(3),240(2009) |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%