为了研究氯化物熔盐对Cr-A1-N涂层热腐蚀性能的影响,采用反应磁控溅射的方法在Ti3Al合金表面制备了Cr082Al0.18N涂层,研究了涂层在Na2SO4+ 25％ K2SO4和Na2SO4+ 25％ NaCl(质量分数)2种熔盐中的热腐蚀行为,采用XRD和SEM分析了涂层热腐蚀产物的相组成和形貌.结果表明:涂层在含有氯化物盐的熔盐中腐蚀时表现为失重而在硫酸盐中腐蚀时表现为增重;Cr0.82Al0.18N涂层在2种熔盐中的腐蚀都主要由Cr2O3和θ-A12O3组成.氯化物熔盐和腐蚀产物的挥发导致了在含有氯化物熔盐中腐蚀时的失重现象.当含有氯化物盐时会增加熔盐中氧离子的活度,从而加速Cr2O3在熔盐中的溶解.此外,热腐蚀过程中产生的氯气也会参与腐蚀反应,从而加速涂层的消耗.
参考文献
| [1] | Kawate M.;Hashimoto AK.;Suzuki T. .Oxidation resistance of Cr1-xAlxN and Ti1-xAlxN films[J].Surface & Coatings Technology,2003(2):163-167. |
| [2] | Zhu M;Li MS;Zhou YC .Oxidation resistance of Cr1-xAlxN (0.18 <= x <= 0.47) coatings on K38G superalloy at 1000-1100 degrees C in air[J].Surface & Coatings Technology,2006(6):2878-2886. |
| [3] | Tsaur CC;Rock JC;Wang CJ;Su YH .The hot corrosion of 310 stainless steel with pre-coated NaCl/Na2SO4 mixtures at 750 degrees C[J].Materials Chemistry and Physics,2005(2/3):445-453. |
| [4] | Li YS;Spiegel M;Shimada S .Corrosion behaviour of various model alloys with NaCl-KCl coating[J].Materials Chemistry and Physics,2005(1):217-223. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%