Ferrous ion was transformed into feroxyhyte (δ-FeOOH) by oxidation. Then, manganese sulfate and zinc sulfate in some ratio were added to the feroxyhyte solution. The co-precipitation was boiling reflux conditions sometime under constant stirring. The nanosize MnZn ferrite powder was formed. The mechanism of preparation of the nanosize MnZn ferrite was discussed, and the formation of feroxyhyte which was playing a key role during the process was mentioned. The properties of powder was tested by means of X-ray diffraction, transmission electron microscopy and vibrating sample magnetometer. The results show that the samples of spherical particles about 20 nm, which have characteristics of ferrimagnetism, has larger saturation magnetization, but the remanent magnetization and coercivity are comparatively smaller. The spinel MnZn ferrite nanosize powder was successfully prepared from δ-FeOOH at low temperature, with low-carbon steel and peroxide as main material.
参考文献
| [1] | 何水校.锰锌铁氧体材料的未来发展动向[J].磁性材料及器件,2001(06):27-30. |
| [2] | 王长振,谭维,周甘宇,章四琪.锰锌铁氧体粉制备技术综述[J].中国锰业,2002(03):37-41. |
| [3] | 都有为.磁性材料进展[J].物理,2000(06):323-332. |
| [4] | Lie CT.;Kuo PC.;Hsu WC.;Chang IJ.;Chen JW. .Effect of Zn doping on the magnetoresistance of sintered Fe3O4 ferrites[J].Journal of Magnetism and Magnetic Materials,2002(1/3):160-163. |
| [5] | 车平,陈博,甘树才.铁氧体磁性材料应用的进展及合成方法[J].世界地质,2000(02):205-208. |
| [6] | 陆明岳.MnZn铁氧体最新进展及其发展趋势[J].磁性材料及器件,2001(05):27-33. |
| [7] | 古映莹,谭小平,桑商斌,刘胜,朱丹,李强.用共沉淀法制备尖晶石型锰锌铁氧体粉体[J].中南工业大学学报(自然科学版),2002(04):364-366. |
| [8] | 张伟南,陈栋华.草酸盐在无机功能材料中的应用[J].中南民族大学学报（自然科学版）,2004(02):29-32,37. |
| [9] | 桑商斌,古映莹,黄可龙.锰锌铁氧体纳米晶的水热法制备及热动力学研究[J].功能材料,2001(01):27-29. |
| [10] | Rath C;Sahu K K;Anand S et al.Preparation and characterization of nanosize Mn-Zn ferrite[J].Journal of Magnetism and Magnetic Materials,1999,202:77. |
| [11] | 余忠,兰中文,王京梅.溶胶-凝胶法制备MnZn铁氧体粉体[J].功能材料,2000(Z1):34. |
| [12] | Yao Z Q;Wang Q;Zhong B .The preparation of ultrafines of MnZn ferrite by supercritical fluid drying[J].Journal of Magnetic Materials and Devices,1998,29(01):6. |
| [13] | Xu K;Liu J J;Xu Z .Synthesis of nanometer-sized zinc ferrite by shock wave treatment method[J].Journal of Inorganic Materials,1997,12(05):759. |
| [14] | Thakur A;Singh M .Preparation and characterization of nanosiz Mn0.4Zn0.6Fe2O4 ferrite by citrate precursor method[J].Ceramics International,2003,29:505. |
| [15] | Ishikawa T;Yasukawa A;Kandori K .Textures of tetradecahedron δ-FeOOH particles and their thermal decomposition products[J].Chemical Society Faraday Transactions,1994,90(17):2567. |
| [16] | Ishikawa T;Cai Y W;Kandori K .Characterization of the thermal decomposition products of δ-FeOOH by fourier-transform infrared spectroscopy and N2 adsorption[J].Chemical Society Faraday Transactions,1992,88(08):1173. |
| [17] | Jiménez M J M;Morales J;Tirado J L .X-ray line broadening in haematite derived from δ-FeOOH by thermal and mechanical procedures[J].Colloid and Interface Science,1988,122:507. |
| [18] | Misawa T .The thermodynamic consideration for Fe-H2O system[J].Corrosion Science,1973,13:659. |
| [19] | Liang W P;Ru Zhuangye;Ke Xue Yu;Ji Shu Ji Chu.[M].北京:科学出版社,2001:105. |
| [20] | Fan Y K .Study on Soft Magnetic Mn-Zn Ferrites with low Temperature Coefficient and Low Coercive Force Prepared by Sol-Gel[D].合肥:安徽大学,2002. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%