介绍了一种制备介孔纳米复合材料的新方法--SiO2溶胶"纳米粘合剂法".应用此方法制备的纳米复合材料是介孔材料,材料具有大比表面积和高空隙率的特点;复合材料中的纳米颗粒或固体微粒保持复合前的形态和大小,没有被包覆而有自由表面并直接同外界环境相通,且可复合量较高.因此,这类纳米复合材料不但具有浸泡法和原位法制备的纳米复合材料的优点,而且克服了这2种方法固有的缺点,在光电材料、特种电荷贮存材料、敏感材料和催化材料方面有着广阔的应用前景.
参考文献
| [1] | DavidMA;Ying Y J .[J].Angewandte Chemie International Edition,1995,34:2014. |
| [2] | Poco JF.;Hrubesh LW.;Satcher JH. .Synthesis of high porosity, monolithic alumina aerogels[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2001(1/3):57-63. |
| [3] | CaiWP;Zhang L D .[J].Journal of Physics:Condensed Matter,1997,9:7257. |
| [4] | CarpenterJP;Lukehart C M;Molne S B .[J].Chemistry of Materials,1997,9:3164. |
| [5] | MorrisAG;ersonLM;Stroud M R .[J].科学（上海),1999,284:622. |
| [6] | AndersonLM;Morris A G;Stroud M R .[J].Langmuir,1999,15:674. |
| [7] | CounioG;Esnouf S;Gacoin T et al.[J].Journal of Physical Chemistry,1996,100:20021. |
| [8] | 冯乙巳 .[D].中国科学院固体物理研究所,2003. |
| [9] | FengYS;Li Y;Zhou S M.Mater Lett 2002[J].Synthesis of SnO2/SiO2 nanocomposite with Large Special Surface Area,2002 |
| [10] | 刘汉范.高分子稳定金属纳米簇的合成及催化研究[J].中国科学院院刊,2001(01):36-38. |
| [11] | KrastevaN;Besnard I;Guse B et al.[J].NANO LETTERS,2002,2:551. |
| [12] | CominiG;Faglia G;Sberveglieri G et al.[J].Applied Physics Letters,2002,81:1869. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%