Hot-pressed sintering was employed to prepare the sodium super ionic conductor (Na1+xZr2SixP3-xO12,1.8≤x≤2.2)ceramics and compare with the sample obtained from normal-press sintering. The phase formation, density, and conductivity of the hot-press sintered and the normal-press sintered samples were investigated in detail. Results show that the density of NASICON ceramics and the degree of crystallization can be improved by hot-press process efficiently. The density of the sample sintered by normal sintering is obviously lower than that sintered by hot press. XRD analysis indicates all the hot press sintered samples contain mainly monoclinic NASICON and no ZrO2 phase was found. The ionic conductivity of normal-press sintered sample is much lower than that of hot-press sintered sample. When the composition is close to Na3Zr2Si2PO12 , the dc conductivities of the hot press sintered samples were in the order of 10-3 S·cm-1.The variation of the ac conductivity with frequency in the high frequency region agrees with the power law feature of σ(ω) ∝ωn(0＜n＜1).
参考文献
| [1] | Lee D D;Choi S D;Lee K W .Carbon dioxide sensor using NASICON prepared by the sol-gel method[J].Sensors and Actuators B-Chemical,1995,24-25:607. |
| [2] | Kida T.;Shimanoe K.;Yamazoe N.;Miyachi Y. .NASICON thick film-based CO2 sensor prepared by a sol-gel method[J].Sensors and Actuators, B. Chemical,2001(1):28-32. |
| [3] | Traversa E.;Sadaoka Y.;Montanaro L.;Aono H. .Electrical properties of sol-gel processed NASICON having new compositions[J].Sensors and Actuators, B. Chemical,2000(1/3):204-208. |
| [4] | Kim J;Oh T;Lee M et al.Effects of Al2O3 addition on the sinterability and ionic conductivity of nasicon[J].Journal of Materials Science,1993,28:1573. |
| [5] | Choy J;Han Y;Kim Y et al.Physico-chemical characterization of Na3Zr2Si2PO12 fine powders prepared by sol-gel method using citrates[J].Japanese Journal of Applied Physics,1993,32:1154. |
| [6] | Kang H;Cho H .Phase formation,sintering behavior,and electrical characteristics of NASICON compounds Influence of microstructure on the electrical properties of NASICON materials[J].Journal of Materials Science,1999,34:5005. |
| [7] | Shimizu Y.;Ushijima T. .Sol-gel processing of NASICON thin film using aqueous complex precursor[J].Solid state ionics,2000(1/2):143-148. |
| [8] | Schaf O;Weibel A;Llewellyn P L et al.Preparation and electrical properties of dense ceramics with NASICON composition sintered at reduced temperatures[J].Journal of Electroceramics,2004,13:817. |
| [9] | 朱棋锋,邱法斌,全宇军,王永为,全宝富,徐宝琨.NASICON纳米晶固体材料的制备与烧结致密化[J].无机材料学报,2004(03):510-516. |
| [10] | Fuentes RO.;Marques FMB.;Franco JI.;Figueiredo FM. .Influence of microstructure on the electrical properties of NASICON materials[J].Solid state ionics,2001(1/2):173-179. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%