采用溶胶-凝胶浸渍提拉法在石英玻璃片上制备了Ag/TiO2薄膜.为研究不同热处理温度(500,600,700℃)对制备过程的影响,在薄膜的制备过程中其他的条件均不变(钛酸丁酯和硝酸银的摩尔比为1:0.18).用透射电子显微镜(Transmission Electron Microscope,TEM)记录样品的透射显微镜图像和衍射花样以表征薄膜的结构,用背散射电子(Backscattered Electron,BSE)检测器观察样品表面的组分分布,用能谱EDAX(Energy Dispersive Analysis of X-rays)分析Ag/TiO2薄膜样品的元素成分组成.实验结果表明,500℃熟处理时得到了含有尺寸均匀的纳米银粒子的Ag/TiO2膜,随着热处理温度的升高,Ag的颗粒逐渐长大,尺寸分布变得不均匀,同时,膜中的银逐渐向薄膜表面迁移并挥发.
参考文献
| [1] | Toshinori T;Takehiro K N;Tomohisa Y et al.[J].Journal of Membrane Science,2006,280:165. |
| [2] | Yu JG;Yu HG;Ao CH;Lee SC;Yu JC;Ho WK .Preparation, characterization and photocatalytic activity of in situ Fe-doped TiO2 thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(2):273-280. |
| [3] | Bessekhouad Y;Robert D;Weber J V .[J].Journal of Photochemistry and Photobiology A:Chemistry,2004,163:569. |
| [4] | Wayne M C;Anthony K B;David L O et al.[J].Coordination Chemistry Reviews,2004,248:1363. |
| [5] | Iketani K;Sun RD;Toki M;Hirota K;Yamaguchi O .Sol-gel-derived VxTi1-xO2 films and their photocatalytic activities under visible light irradiation[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2004(3):187-193. |
| [6] | Shinya O Y M;Masato U .[J].Journal of Photochemistry and Photobiology A:Chemistry,2004,168:1. |
| [7] | 高濂;郑珊;张青红.纳米氧化钛光催化材料及应用[M].北京:化学工业出版社,2002 |
| [8] | 张彭义;余刚;蒋展鹏 .[J].环境科学进展,1997,5(03):1. |
| [9] | 国伟林,杜红,王西奎.掺银二氧化钛的超声化学法制备与光催化性能研究[J].济南大学学报(自然科学版),2004(04):301-303. |
| [10] | 苏会东,刘瑛,魏守强,邵忠财,翟玉春.光沉积银微弧氧化TiO2膜光催化杀菌研究[J].表面技术,2006(01):25-27,59. |
| [11] | Tan T T Y;Noritsugu K;Tomoko S et al.[J].CHEMICAL ENGINEERING JOURNAL,2003,95:179. |
| [12] | 姚平平,甘玉琴,徐景坤,杨平,杜玉扣.银纳米颗粒负载TiO2复合薄膜的光催化活性及其光电流性质[J].感光科学与光化学,2006(01):44-49. |
| [13] | Zhao G L;Kozuka H;Yoko T .[J].Thin Solid Films,1996,277:147. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%