研制了一种含钛镍基合金,并采用X射线衍射(XRD)、扫描电镜(SEM)及能谱(EDS)等手段研究了其在850℃和950℃熔融硫酸盐中的热腐蚀行为.结果表明,热腐蚀期间,合金发生了氧化、硫化现象,合金表面腐蚀产物层可分为3层,外氧化层以Al2O3、Cr2O3和Cr2O4相为主,中间层为Al2O3相,内层为CrS和Ti2S硫化物层;随腐蚀温度提高合金表面腐蚀层的厚度增加,合金内氧化物区域和内硫化物区域加深.
参考文献
| [1] | Xinyue Wang,Li Xin,Fuhui Wang,Shenglong Zhu,Hua Wei,Xiaolan Wang.Influence of Sputtered Nanocrystalline Coating on Oxidation and Hot Corrosion of a Nickel-based Superalloy M951[J].材料科学技术（英文版）,2014(09):867-877. |
| [2] | 卢旭东,田素贵,王涛,朱德刚.溅射NiCrAlY纳米晶涂层在900℃的热腐蚀行为[J].材料热处理学报,2013(10):153-159. |
| [3] | 卢旭东,田素贵,陈涛,郭策安,李光瑞.高铬镍基合金熔融硫酸盐热腐蚀过程中内氧化和内硫化行为的研究[J].稀有金属材料与工程,2014(01):79-84. |
| [4] | Das S;Datta S;Basu D et al.Hot corrosion of galss coating on nickel based superalloy[J].Ceramics International,2008,34:1217-1218. |
| [5] | Zhao S Q;Xie X S;Gaylord D S .The oxidation behavior of the new nickel-based superalloy Inconel 740 with and without Na2SO4 deposit[J].Surface and Coatings Technology,2004,185:181-182. |
| [6] | 田素贵,卢旭东,孙振东.高Cr镍基合金的高温内氧化和内氮化行为[J].中国有色金属学报,2012(02):408-415. |
| [7] | Lu X D;Tian S G;Shui L et al.Oxidation of behavior of a Ni-based superalloy in air at 800 ℃[J].Journal of Iron and Steel Research,2010,17:98-100. |
| [8] | Ren X;Wang F H .High-temperature oxidation and hot-corrosion behaviour of a sputtered NiCrAlY coating with and without aluminizing[J].Surface and Coatings Technology,2006,201:34-35. |
| [9] | Ren X;Wang F H;Wang X .High-temperature oxidation and hot corrosion behaviors of the NiCr-CrAl coating on a nickel-based superalloy[J].Surface and Coatings Technology,2005,198:429-430. |
| [10] | Zhang K;Liu M M;Liu S L et al.Hot corrosion behaviour of a cobalt-base super-alloy K40S with and without NiCrAlYSi coating[J].Corrosion Science,2011,53:1995-1996. |
| [11] | 卢旭东,田素贵,于兴福,王常鑫.Ni-Cr-Ta-Al-Co-Mo合金在900℃和1000℃的恒温氧化行为[J].材料研究学报,2011(04):427-432. |
| [12] | 李维杰,刘咏,王岩,韩朝,汤慧萍.Ni-16Cr-xAl合金在600℃ Na2SO4-NaCl混合盐中的热腐蚀行为[J].中国有色金属学报（英文版）,2011(12):2617-2625. |
| [13] | Wang H Y;Zuo D W;Chen G et al.Hot corrosion behaviour of low Al NiCoCrAlY cladded coatings reinforced by nano-particles on a Ni-base super alloy[J].Corrosion Science,2010,52:3564-3565. |
| [14] | Zheng L;Zhang M C;Dong J X .Hot corrosion behavior of powder metallurgy Rene95 nickel-based superalloy in molten NaCl-Na2SO4 salts[J].Materials and Design,2011,32:1985-1986. |
| [15] | Chen L C;Zhang C;Yang Z G .Effect of pre-oxidation on the hot corrosion of CoNiCrAlYRe alloy[J].Corrosion Science,2011,53:377-378. |
| [16] | 韩朝,刘咏,王岩,李维杰,汤慧萍.Ni-xCr-6.8Al基合金热腐蚀行为[J].中国有色金属学报（英文版）,2011(11):2348-2357. |
| [17] | Yu P;Wang W;Wang F H et al.High-temperature corrosion behavior of sputtered K38 nanocrystalline coatings with and without yttrium addition in molten sulfate at 900 ℃[J].Surface and Coatings Technology,2011,206:72-73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%