本文通过对碳氮共渗齿轮材料接触疲劳性能试验和接触表面剥落过程的断裂力学分析及裂纹顶端塑性区的能量计算,研究了表层组织中的残留奥氏体在提高此类材料接触疲劳强度中所起的作用。
A study was made of the behaviour of retained austenite to improve the contact fatigue strength of the carbonitriding gear steel 25MnTiBR by means of the contact fatigue test, the fracture mechanics analysis of spalling on contact surface and the energy estimation of crack tip plastic zone The retained austenite deformation induces the martensite transformation, which absorbs energy more than one half of the strain energy of material It may retard the propagation of fatigue cracking and may improve the contact fatigue strength of the carbonitriding steel 25MnTiBR with retained austenite The proper material together with a reasonable technique chosen for production practice may be available to obtain more and not very stable retained austenite in the surface layer of the gear, especially, it may improve the gears under heavy load.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%