研究了TiO气凝胶形成过程中制备条件和凝胶化过程对块状TiO气凝胶宏观性质的影响,结果表明所得气凝胶是由粒度约为4~6nm的TiO非晶态微粒连结而成的具有均匀网络结构的多孔性超轻量级块状材料,通过严格控制制备过程中凝胶化过程的条件及状态,可以获得不同密度不同品质的TiO气凝胶.

Monolithic TiO2 aerogels were prepared by the process of hydrolysis and condensation of tetrabutyl titanate as precursor, and following by supercritical
drying. The effect of the preparing conditions and gelation process on macroscopic properties of monolithic TiO2 aerogels was studied. The results indicate
that the final aerogels, which consist of amorphous TiO2 with particle sizes of about 4-6nm, are uniform continuous network structural superlight monolithic materials with high porosity. The monolithic TiO2 aerogels with different densities
and properties can be prepared by controlling the conditions of gelation process vigorously.

参考文献

[1] Matijevic E, Meites L. J. Colloid Interface Sci., 1977, 16 (2): 4305--4310.
[2] Anpo M, Shima T, Kodama S, et al. J. Phys. Chem., 1987, 91 (16): 302--311.
[3] 张青红, 高濂, 郭景坤(ZHANG Qing-Hong, et al). 无机材料学报(Journal of Inorganic Materials?) 2000, 15 (3): 29--35.
[4] Dagan G, Tomkiewicz M. Journal of Non-crystalline Solids, 1994, 175: 294--302.
[5] 张敬畅, 曹维良, 于定新, 等(ZHANG Jing-Chang, et al). 无机材料学报(Journal of Inorganic Materials), 1999, 14 (1): 29--35.
[6] 陈龙武, 甘礼华, 徐子颉 (CHEN Long-Wu, et al). 高等学校?化学学报 (Chemical Journal of Chinese Universities)(待发表).
[7] 沈军, 王珏, 甘礼华, 陈龙武(SHEN Jun, et al). 无机材料学报 (Journal of Inorganic Materials)?, 1995, 10 (1): 69--75.
[8] 胡黎明, 顾燕芳, 顾家建, 等 (HU Li-Ming, et al). 华东化工学院学报 ( Journal of East China Institute of Chemical Technology )?, 1990, 16 (3): 265--269.
[9] 陈奇, 崔景巍, 宋鹂, 等 (CHEN Qi, et al). 无机材料学报 ( Journal of Inorganic Materials )?, 1991, 6 (2): 249--255.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%