研究了催化剂、固化时间和温度对环氧树脂(EP)或丁腈橡胶(A)改性氰酸酯树脂(CE)固化反应的影响以及CE/A膜性能.不舍催化剂的CE/EP体系160℃不能有效固化,而含有二月桂酸二丁基锡(B)的CE/EP体系能有效固化,且固化反应速度随着B用量增加而提高.CE/A/B体系的固化程度随着固化时间延长和温度升高而提高.CE/EP/B体系的固化温度比CE/EP体系明显降低,其下降幅度随着B用量增加而提高.CE/A/B体系固化温度比CE/EP/B体系低.A用量增加,改性CE膜的冲击强度和柔韧性提高,但它的热分解温度和抗湿性下降.
参考文献
| [1] | Mathew D.;Ninan KN.;Nair CPR. .Effect of polymeric additives on properties of glass-bisphenol A dicyanate laminate composites[J].Journal of Applied Polymer Science,2000(1):75-88. |
| [2] | Boey FYC.;Qiang W. .Experimental modeling of the cure kinetics of an epoxy-hexaanhydro-4-methylphthalicanhydride (MHHPA) system[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(6):2081-2094. |
| [3] | 孟季茹,梁国正,赵磊.傅立叶红外光谱法研究氰酸酯树脂及其改性体系的固化反应[J].高分子材料科学与工程,2003(02):180-183. |
| [4] | Hayes BS.;Parker GA.;Seferis JC. .Rubber modification of low temperature cure cyanate ester matrices and the performance in grass fabric composites[J].Polymer engineering and science,2000(6):1344-1349. |
| [5] | Maya EM.;Snow AW.;Buckley LJ. .Oligodimethylsiloxane linked cyanate ester resins[J].Macromolecules,2002(2):460-466. |
| [6] | 赵磊,梁国正,孟季茹,秦华宇.用于RTM工艺的改性氰酸酯树脂的研究[J].高分子材料科学与工程,2001(06):175-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%