实验以石灰中和后的磷石膏为原料,分别以顺丁烯二酸、氨三乙酸、丁二酸为晶形控制剂,采用“半液相法”制备α半水石膏.利用XRD、SEM、XRF及EDS分别对原料及α半水石膏的物相组成、结晶形貌、成分含量等特征进行表征.结果表明:晶形控制剂在改善α半水石膏晶体形貌的同时并没有改变晶体的物相组成,可以有效抑制晶体一维方向的生长,生成短柱状的α半水石膏晶体.其中顺丁烯二酸用量在0.1％,制备的α半水石膏结晶形态最好,长径比接近1∶1,转化率可达到98％.抗压强度可达45.3 MPa.
参考文献
| [1] | 张巨松;郑万荣;陈华;张添华;王文军;金建伟;张伯勋.影响α半水石膏粒度、形貌及强度的因素[J].沈阳建筑大学学报（自然科学版）,2006(6):930-934. |
| [2] | Chen, J.;Gao, J.;Yin, H.;Liu, F.;Wang, A.;Zhu, Y.;Wu, Z.;Jiang, T.;Qin, D.;Chen, B.;Ji, Y.;Sun, M..Size-controlled preparation of α-calcium sulphate hemihydrate starting from calcium sulphate dihydrate in the presence of modifiers and the dissolution rate in simulated body fluid[J].Materials science & engineering, C. Materials for Biogical applications,20136(6):3256-3262. |
| [3] | 郑万荣;张巨松;杨洪永;张添华;王文军;金建伟.转晶剂、晶种和分散剂对α半水石膏晶体粒度、形貌的影响[J].非金属矿,2006(4):1-4. |
| [4] | 杨林;刘亚明;周杰;林倩.磷石膏制备α型高强石膏转晶剂的研究[J].非金属矿,2014(1):22-24. |
| [5] | 彭家惠;张建新;瞿金东;陈明凤;万体智.有机酸对α半水脱硫石膏晶体生长习性的影响与调晶机理[J].硅酸盐学报,2011(10):1711-1718. |
| [6] | 白杨;李东旭.用脱硫石膏制备高强石膏粉的转晶剂[J].硅酸盐学报,2009(7):1142-1146. |
| [7] | 杨兆娟;王海晏;向兰.利用水热法对磷石膏进行除杂脱水的工艺探讨[J].青海大学学报（自然科学版）,2007(2):44-47. |
| [8] | 何玉龙;陈德玉;刘路珍;王舒州;刘成.磷石膏制备高强石膏工艺研究[J].非金属矿,2015(2):1-4. |
| [9] | Development of alpha plaster from phosphogypsum for cementitious binders[J].Construction and Building Materials,200910(10):3220-3224. |
| [10] | 张巨松;郑万荣;范兆荣;高飞;邓嫔;孙蓬.α半水石膏晶体生长习性的探讨[J].沈阳建筑大学学报（自然科学版）,2008(2):261-264. |
| [11] | 杨林;周杰;李贺军;曹建新.晶形助长剂对磷石膏制硫酸钙晶须性能的影响[J].无机盐工业,2012(10):41-43. |
| [12] | 牟国栋.半水石膏水化过程中的物相变化研究[J].硅酸盐学报,2002(04):532-536. |
| [13] | Baohong Guan;Li Yang;Hailu Fu.α-calcium sulfate hemihydrate preparation from FGD gypsum in recycling mixed salt solutions[J].Chemical engineering journal,20111(1):296-303. |
| [14] | Badens E.;Fulconis JM.;Jourdan C.;Veesler S.;Boistelle R.;Rouquerol F.;Llewellyn P..Study of gypsum dehydration by controlled transformation rate thermal analysis (CRTA)[J].International Journal of Quantum Chemistry,19981(1):37-44. |
| [15] | N.B. Singh;B. Middendorf.Calcium sulphate hemihydrate hydration leading to gypsum crystallization[J].Progress in Crystal Growth and Characterization of Materials,20071(1):57-77. |
| [16] | 彭家惠;王凤仙;张建新;吴莉;谢厚礼.柠檬酸对石膏析晶过饱和度和微结构的影响[J].武汉理工大学学报,2006(11):44-47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%