Duplex stainless steels are gaining global importance because of the need for a high strength corrosion resistant material. Three compositions of this group were selected with three different nitrogen contents viz, 0.15 wt pct (alloy 1), 0.23 wt pct (alloy 2) and 0.32 wt pct (alloy 3). The steels were melted in a high frequency induction furnace and hot forged to various reductions from 16% to 62%. In this work, the effect of hot forging on the ferrite content, hardness, yield strength, impact strength and grain orientation (texture) were studied. Fracture analysis on all the forged specimens using SEM reveals that a size reduction of 48% results in maximum ductility and impact strength as well as minimal ferrite content and grain size. Thus the mechanical properties are found to have a direct correlation to ferrite content and grain size. The highest impact strength was observed in specimens with the smallest grain size, which was observed in specimens forged to 48% reduction in size.
参考文献
| [1] | T Havn;A Morini;H Salbu;O Strandmyr.[A].Maastricht,Netherlands,1997:191. |
| [2] | J Charles.[A].Beaune,France,1991:43. |
| [3] | J O Nilsson .[J].Materials Science and Technology,1992,8:685. |
| [4] | M.Sagradi;D.Pulino-Sagraki;R.E.Medrano .The effect of the microstructure on the superplasticity of a duplex stainless steel[J].Acta materialia,1998(11):3857-3862. |
| [5] | Francois Millet Jean-marc;Pugnet Angelo Franzi;Bernard Bonnefois;Jean-marc Lardon.[A].Maastricht,Netherlands,1997:713. |
| [6] | J M Lardon;R CozarR.[A].Maastricht,Netherlands,1997:147. |
| [7] | Komi Jukka .[D].University of Oulu,Oulu,2001. |
| [8] | Johan J Moveare;Magnus Oden .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2002,33A:57. |
| [9] | W Horvath;W Prantl;H StroiBnigg;E A Werner .[J].Material Science and Engineering,1998,A256(227) |
| [10] | I Samajdar;P Ratchev;B Verlinden;E Aernoudt .[J].Acta Matter,2001,49(1759) |
| [11] | M Kiran Kumar;I Samajdar;N Venkatramani;G K Dey,R Tewari,D Srivastava and S Banerjee .[J].Acta Materialia,2003,625(51) |
| [12] | P. Chandramohan;S.S. Mohamed Nazirudeen;R. Srivatsavan .The effect of nitrogen solubility, heat treatment and hot forging on 0.15%N duplex stainless steels[J].International journal of materials & product technology,2006(4):281-296. |
| [13] | K AYushchenko;A K Avdeeva;Yu N Kakhovsky.[A].Maastricht,Netherlands,1997:911. |
| [14] | A Jimenez;F Carreno;O A Ruano;M Carsi .[J].Materials Science and Technology,1999,15:127. |
| [15] | F E A1 Jouni;C M Sellars .[J].Materials Science and Technology,2003,19:1311. |
| [16] | G S Reis;A M Jorge Jr;O Balancin .[J].Mater Res,2000,31(02):3. |
| [17] | M Vedani Nicodemi;E Gariboldi;W Nicodemi;R Roberti.[A].Maastricht,Netherlands,1997:245. |
| [18] | Kuang Liang Weng;Tung Hung Chen;Jer Ren Yang.Bull.College Eng[M].National Taiwan University,2003:45. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%