利用高温固相分段加热法合成锂锰氧正极材料LiMn0.9Mo0.1 O2,并对其进行了常温充放电、循环伏安、交流阻抗、电镜扫描等电化学性能测试.在2.0～4.3V电压范围内,其首次充电容量为160mAh/g,放电容量为158mAh/g;经10次充放电循环后,其充电容量为156mAh/g,放电容量为155 mAh/g(对极为锂片);经SEM检测,该正极材料主要为正交型锂锰氧化物.
参考文献
| [1] | Guo Z P;Zhong S;Wang S X et al.[J].Journal of Alloys and Compounds,2003,348:231-235. |
| [2] | Guo ZP.;Wang GX.;Liu HK.;Dou SX. .Structure and electrochemistry of LiCrxMn1-xO2 cathode for lithium-ion batteries[J].Solid state ionics,2002(3/4):359-366. |
| [3] | Wei Min;Lu Yanluo;Evans D G et al.[J].Solid State Ionics,2003,161:133-144. |
| [4] | 吴宇平,李阳兴,万春荣,姜长印.锂离子二次电池正极材料氧化锰锂的研究进展[J].功能材料,2000(01):18-22. |
| [5] | Davidson I J;McMillan R S;Murray J J et al.[J].Journal of Power Sources,1995,54:232-235. |
| [6] | Park K S;Cho M H;Park S H et al.[J].Electrochimica Acta,2002,47:2937-2942. |
| [7] | Komaba S.;Myung ST.;Kumagai N.;Kanouchi T.;Oikawa K.;Kamiyama T. .Hydrothermal synthesis of high crystalline orthorhombic LiMnO2 as a cathode material for Li-ion batteries[J].Solid state ionics,2002(Pt.A):311-318. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%