流动加速腐蚀(FAC)是核电厂二回路管线最主要的失效原因之一,严重影响核安全运行.CH ECWORKS 是美国电力研究院(EPRI)基于FAC经验模型设计开发的商用计算机程序,用以预测FAC速率及其相关的水化学、热工水力参数等.从发展历史、应用现状、程序特点等方面对CHECWORKS进行了综述,为该程序在我国的推广以及在核电厂老化管理中的应用起到积极作用.
参考文献
| [1] | Vivekanand Kain;S. Roychowdhury;P. Ahmedabadi .Flow accelerated corrosion: Experience from examination of components from nuclear power plants[J].Engineering failure analysis,2011(8):2028-2041. |
| [2] | Kain, V;Roychowdhury, S;Mathew, T;Bhandakkar, A .Flow accelerated corrosion and its control measures for the secondary circuit pipelines in Indian nuclear power plants[J].Journal of Nuclear Materials,2008(1/2):86-91. |
| [3] | 杨振国.核电装置换热器的失效分析及其解决对策[J].金属热处理,2007(z1):28-35. |
| [4] | V. I. Baranenko;A. V. Kumov;Yu. A. Yanchenko;A. S. Prokopenko .Development of Software Tools for Calculating Corrosion-Erosion Wear of Pipelines at Nuclear Power Stations[J].Thermal engineering,2007(12):981-988. |
| [5] | R. B. Dooley;V. K. Chexal .Flow-accelerated corrosion of pressure vessels in fossil plants[J].International Journal of Pressure Vessels and Piping,2000(2/3):85-90. |
| [6] | 张桂英,顾宇,邵杰.核电站汽水管道流动加速腐蚀的影响因素分析及对策[J].动力工程学报,2012(02):170-176. |
| [7] | 刘春波,郑玉贵.核电行业中流动促进腐蚀的模型和数值模拟研究进展[J].腐蚀科学与防护技术,2008(06):436-439. |
| [8] | G.V.Tomarov;A.A.Shipkov .Principles of Development and Specific Features Relating to Practical Application of Software for Solving Problems Connected with Erosion—Corrosion of Metal in Power Engineering[J].Thermal engineering,2011(2):135-142. |
| [9] | 束国刚,薛飞,遆文新,汪小龙,陆念文,刘鹏,戴忠华.核电厂管道的流体加速腐蚀及其老化管理[J].腐蚀与防护,2006(02):72-76. |
| [10] | 龚嶷 .石化、火电工业用换热管的腐蚀失效分析及其性能评价[D].复旦大学,2012. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%