研究了不同程度渗氢处理Zr-4合金的双轴循环变形行为.结果表明:当氢含量为CH=400μg/g时,在相同等效应变幅和相同相位角下,渗氢Zr-4合金的疲劳寿命高于原始冷变形状态Zr-4合金.当氢含量增加到CH=580μg/g时,渗氢处理Zr-4合金的双轴疲劳寿命却低于原始冷变形状态的Zr-4合金.透射电镜和金相显微镜观察表明,冷变形Zr-4合金渗氢后析出的氢化物具有良好的塑性变形能力.渗氢过程中中温条件下长时间保持导致基体产生去应力退火效应是Zr-4合金疲劳寿命提高的主要原因.
参考文献
| [1] | Shi S Q;Pals M P;Sagar S .[J].Journal of Nuclear Materials,1991,20:343. |
| [2] | Shi S Q;Pals M P .[J].Journal of Nuclear Materials,1991,20:232. |
| [3] | Baornclough K G;Reevcr C J .[J].Journal of Mater Scr,1964,4:518. |
| [4] | Kurods M;Yosinicka K;Yamanak S .[J].Journal of Nucl Scr Technol,2000,47:670. |
| [5] | Berlolino G;Meyer G;Perez Ipina J .[J].Journal of Nuclear Materials,2003,320:272. |
| [6] | Yamanaka S;Yoshioka K;Uno M et al.[J].Journal of Alloys and Compounds,1999,293(01):23. |
| [7] | Xiao L;Umakoshi Y;Sun J .[J].Metallurgical and Materials Transactions,2001,32A:2841. |
| [8] | 丁向东,王瑞红,刘刚,肖林,孙军.渗氢后再结晶状态Zr-4合金拉伸变形的原位观察[J].金属学报,2003(03):267-272. |
| [9] | Arsene S;Bai J B;Bompard P .[J].Metallurgical and Materials Transactions,2003,34:553. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%