通过对高碳盘条内部缺陷的假设,采用有限元法研究了高碳盘条拉拔过程中,工艺参数对裂纹扩展情况的影响.研究结果表明,针对1 860 MPa级PC钢绞线用热轧高碳盘条的拉拔生产,其最佳拉拔角约为8°.对于相同尺寸的裂纹,J积分值随着模具顶角的增大而增加;当模具顶角小于8°后,J积分值变化较小,趋于一定值;J积分值随着摩擦系数的增大而增大;芯部缺陷的临界尺寸为30～40μm.计算结果得到了试验结果的初步验证.
参考文献
| [1] | John A Schey .Speed Effects in Drawbead Simulation[J].Journal of Materials Processing Technology,1996,57(01):146-154. |
| [2] | Brethenoux G;Bourgain E;Pierson G et al.Cold Forming Processes:Some Examples of Predictions and Design Optimization Using Numerial Simulations[J].Journal of Materials Processing Technology,1996,60(03):555-562. |
| [3] | Aly El-Domiaty;Sadek Z. Kassab .Temperature rise in wire-drawing[J].Journal of Materials Processing Technology,1998(1/3):72-83. |
| [4] | Takanari Hamada;Tetsuya Hirouchi;Masayoshi Akiyama .A numerical study on the distribution of temperature in a fine high carbon steel wire subjected to high-speed drawing[J].Wire Journal International,2001(5):86-92. |
| [5] | Ulrich T Riedel;Wolfgang Bleck;John E Morgan.Finite Element Modeling of the Effect of Non-metallic inclusions in Metal Forming Processes[J].Computational Materials Science,1999(16):32-38. |
| [6] | 徐贵娥,孙正华,方峰,李兆霞,蒋建清.拉丝过程中的缺陷模拟及其在拉拔工艺优化中的应用[J].东南大学学报（自然科学版）,2005(03):409-414. |
| [7] | 方峰,涂益友,徐忠良,于金,蒋建清.SWRH82B高碳盘条显微组织对断裂韧性JIC的影响[J].理化检验-物理分册,2005(03):109-112. |
| [8] | 方峰 .小方坯连铸连轧1860MPa级PC钢绞线用热轧盘条的组织与性能[D].东南大学,2003. |
| [9] | 董岩,方峰,蒋建清,顾菡妍,涂益友.高碳热轧盘条中的带状组织及其对拉丝变形行为的影响[J].机械工程材料,2005(08):9-12. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%